General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.13 g/cm³ Show Material materials with Density of 1.13 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.2 % Show Material materials with Water absorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Material materials with Elastic modulus of 2.3 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 10 % Show Material materials with Elongation of 10 % | ISO 527 | 50 mm/min |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ISO 527 | 50 mm/min |
Flexural modulus | 23.0 °C | 2.4 GPa Show Material materials with Flexural modulus of 2.4 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 81 MPa Show Material materials with Flexural yield strength of 81 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 93 MPa Show Material materials with Hardness, Ball Indentation of 93 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 116 [-] Show Material materials with Hardness, Rockwell R of 116 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -30.0 °C | 20 kJ/m² Show Material materials with Impact strength, Charpy notched of 20 kJ/m² | ISO 179/1eA |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy notched of 45 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -30.0 °C | 20 kJ/m² Show Material materials with Impact strength, Izod notched of 20 kJ/m² | ISO 180/1A |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod notched of 45 kJ/m² | ISO 180/1A | |
Tensile strength | 23.0 °C | 45 MPa Show Material materials with Tensile strength of 45 MPa | ISO 527 | 50 mm/min |
Yield strength | 23.0 °C | 50 MPa Show Material materials with Yield strength of 50 MPa | ISO 527 | 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8E-5 1/K Show Material materials with Coefficient of thermal expansion of 8E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 97 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 97 °C | ISO 75/Ae | 1.8 MPa | |||
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 124 °C Show Material materials with Vicat softening temperature of 124 °C | ISO 306 | Rate B/120 | |||
Flammability | FMVSS Burning Speed, thickness 1 mm | 35mm/min | FMVSS 302 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 275 V Show Material materials with Comparative tracking index of 275 V | IEC 60112 |
Dielectric constant | 23.0 °C | 2.6 [-] Show Material materials with Dielectric constant of 2.6 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 9E-3 [-] Show Material materials with Dissipation factor of 9E-3 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 20 cm³/10min Show Material materials with Melt volume-flow rate of 20 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Air Conditioning,Audio,Auto Aftermarket,Body Protection,Cladding,Cluster,Console,Data Management,Data Transfer,Defense Vehicles,Dishwasher,Displays,Document Handling,Doors Hardware/Trim,Electronic Components,Enclosure/Housing/Cover,Enclosures,EV Infrastructure,Exterior,Forward Lighting,Freezer,Glove Box,Headliner,Infotainment/Telematic,Interior,Medical Device,Neighborhood Electric Vehicle,Non-LED Lighting,Overhead,Personal Computing,Rear/Signal Lighting,Recreational Vehicle,Seat,Small Appliance,Storage/Table,Structure,Trim,Wireless Communications | |
Processing methods | Drying Temperature: 95-105°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 275-300°C, Nozzle Temperature: 275-300°C, Front - Zone 3 Temperature: 260-300°C, Middle - Zone 2 Temperature: 255-295°C, Rear - Zone 1 Temperature: 250-290°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C |