General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.34 g/cm³ Show Material materials with Density of 1.34 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.15 % Show Material materials with Water absorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongation | 23.0 °C | 74 % Show Material materials with Elongation of 74 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.73 GPa Show Material materials with Flexural modulus of 2.73 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural yield strength | 23.0 °C | 97 MPa Show Material materials with Flexural yield strength of 97 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 135 J/m Show Material materials with Impact strength, Izod notched, ASTM of 135 J/m | ASTM D 256 |
23.0 °C | 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2130 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 2130 J/m | ASTM D 4812 |
Tensile strength | 23.0 °C | 50 MPa Show Material materials with Tensile strength of 50 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 57 MPa Show Material materials with Yield strength of 57 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 6.1E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.4E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 129 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Vicat softening temperature | 147 °C Show Material materials with Vicat softening temperature of 147 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94HB Flame Class Rating | 1.5mm | UL 94 | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 7.5 g/10min Show Material materials with Melt mass-flow rate of 7.5 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.8 - 1 % Show Material materials with Shrinkage of 0.8 - 1 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | LED Lighting | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 310-330°C, Nozzle Temperature: 305-325°C, Front - Zone 3 Temperature: 310-330°C, Middle - Zone 2 Temperature: 300-320°C, Rear - Zone 1 Temperature: 290-310°C, Mold Temperature: 80-115°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |