LEXAN™ Resin LUX2289

Want to keep this datasheet? Save it now in your required format

Description

LEXAN LUX2289 resin is an injection molding grade with high light reflectance

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.34 g/cm³

Show Material materials with Density of 1.34 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.15 %

Show Material materials with Water absorption of 0.15 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

120 %

Show Material materials with Elongation of 120 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

6 %

Show Material materials with Elongation at yield of 6 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.5 GPa

Show Material materials with Flexural modulus of 2.5 GPa

ISO 178

Flexural strength

23.0 °C

70 MPa

Show Material materials with Flexural strength of 70 MPa

ISO 178

Flexural yield strength

23.0 °C

98 MPa

Show Material materials with Flexural yield strength of 98 MPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Impact strength, Charpy notched

-30.0 °C

12 kJ/m²

Show Material materials with Impact strength, Charpy notched of 12 kJ/m²

ISO 179/1eA

23.0 °C

67 kJ/m²

Show Material materials with Impact strength, Charpy notched of 67 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

-30.0 °C

140 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 140 kJ/m²

ISO 179/1eU

23.0 °C

140 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 140 kJ/m²

ISO 179/1eU

Unlock all property charts

Impact strength, Izod notched

-30.0 °C

13 kJ/m²

Show Material materials with Impact strength, Izod notched of 13 kJ/m²

ISO 180/1A

23.0 °C

52 kJ/m²

Show Material materials with Impact strength, Izod notched of 52 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-30.0 °C

165 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 165 J/m

ASTM D 256

23.0 °C

648 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 648 J/m

ASTM D 256

Unlock all property charts

Impact strength, Izod unnotched

-30.0 °C

160 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 160 kJ/m²

ISO 180/1U

23.0 °C

170 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 170 kJ/m²

ISO 180/1U

Unlock all property charts

Impact strength, Izod unnotched, ASTM

23.0 °C

2130 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 2130 J/m

ASTM D 4812

Tensile strength

23.0 °C

61 MPa

Show Material materials with Tensile strength of 61 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

60 MPa

Show Material materials with Yield strength of 60 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6E-5 1/K

Show Material materials with Coefficient of thermal expansion of 6E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6.3E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 6.3E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

124 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 124 °C

ASTM D 648 | 1.82 MPa, 3.2mm, unannealed

Vicat softening temperature

142 °C

Show Material materials with Vicat softening temperature of 142 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94V-2 Flame Class Rating | 1.5mm | UL 94

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

17 g/10min

Show Material materials with Melt mass-flow rate of 17 g/10min

ASTM D 1238 | 300°C/1.2 kg

Melt volume-flow rate

16 cm³/10min

Show Material materials with Melt volume-flow rate of 16 cm³/10min

ISO 1133 | 300°C/1.2 kg

Shrinkage

23.0 °C

0.5 - 0.7 %

Show Material materials with Shrinkage of 0.5 - 0.7 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Displays,Enclosures,Forward Lighting,Rear/Signal Lighting

Processing methods

Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-305°C, Nozzle Temperature: 275-300°C, Front - Zone 3 Temperature: 280-305°C, Middle - Zone 2 Temperature: 270-295°C, Rear - Zone 1 Temperature: 260-280°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm