Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.2 g/cm³ Show Material materials with Density of 1.2 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.13 % Show Material materials with Water absorption of 0.13 % | ISO 62 | 23°C, 50% RH |
Water absorption, equilibrium | 100.0 °C | 0.58 % Show Material materials with Water absorption, equilibrium of 0.58 % | ASTM D 570 |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Material materials with Elastic modulus of 2.3 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 100 % Show Material materials with Elongation of 100 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ISO 527 | 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.25 GPa Show Material materials with Flexural modulus of 2.25 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 94 MPa Show Material materials with Flexural yield strength of 94 MPa | ISO 178 | 2 mm/min | ||
Hardness, Rockwell M | 23.0 °C | 70 [-] Show Material materials with Hardness, Rockwell M of 70 [-] | ASTM D 785 | ||
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 | ||
Impact strength, Charpy notched | -30.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | ||
23.0 °C | 63 kJ/m² Show Material materials with Impact strength, Charpy notched of 63 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -30.0 °C | 11 kJ/m² Show Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180/1A | ||
23.0 °C | 60 kJ/m² Show Material materials with Impact strength, Izod notched of 60 kJ/m² | ISO 180/1A | |||
Impact strength, Izod notched, ASTM | 23.0 °C | 650 J/m Show Material materials with Impact strength, Izod notched, ASTM of 650 J/m | ASTM D 256 | ||
Tensile strength | 23.0 °C | 65 MPa Show Material materials with Tensile strength of 65 MPa | ISO 527 | 50 mm/min | ||
Yield strength | 23.0 °C | 63 MPa Show Material materials with Yield strength of 63 MPa | ISO 527 | 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No Break @ 23,-30°C| ISO 180/1U | ||||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 | ||||
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.84E-5 1/K Show Material materials with Coefficient of thermal expansion of 6.84E-5 1/K | ASTM E 831 | -40°C to 95°C | ||
Heat deflection temperature, 1.80 MPa | 123 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 123 °C | ISO 75/Af | 1.8 MPa | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 125 °C Show Material materials with Relative temperature index, mechanical impact of 125 °C | UL 746B | |||
Relative temperature index, mechanical strength | 125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746B | |||
Specific heat capacity | 23.0 °C | 1260 J/(kg·K) Show Material materials with Specific heat capacity of 1260 J/(kg·K) | ASTM C 351 | ||
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ASTM C177 | ||
Vicat softening temperature | 144 °C Show Material materials with Vicat softening temperature of 144 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94V-2 Flame Class Rating | 0.75mm | UL 94 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 3 V Show Material materials with Comparative tracking index of 3 V | UL 746A |
Dielectric constant | 23.0 °C | 2.96 [-] Show Material materials with Dielectric constant of 2.96 [-] | ASTM D 150 | at 1 MHz |
Dielectric strength | 23.0 °C | 15 kV/mm Show Material materials with Dielectric strength of 15 kV/mm | ASTM D 149 | in air, 3.2 mm |
Dissipation factor | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor of 0.01 [-] | ASTM D 150 | at 1 MHz |
Optical
| Property | Value | Comment |
|---|---|---|
Refractive index | 1.59 [-] Show Material materials with Refractive index of 1.59 [-] | ISO 489 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt volume-flow rate | 7 cm³/10min Show Material materials with Melt volume-flow rate of 7 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Air Conditioning,ATM/Ticket Machine,Coffee Maker/Espresso Machine,Data Transfer,Electronic Components,Enclosures,LED Lighting,Personal Computing,Wearables,Wireless Communications | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-300°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-100°C | |