General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.14 g/cm³ Show Material materials with Density of 1.14 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.1 % Show Material materials with Water absorption of 0.1 % | ASTM D 570 | 24 Hours |
Water absorption, equilibrium | 23.0 °C | 0.4 % Show Material materials with Water absorption, equilibrium of 0.4 % | ASTM D 570 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 2.2 GPa Show Material materials with Elastic modulus of 2.2 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 150 % Show Material materials with Elongation of 150 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.34 GPa Show Material materials with Flexural modulus of 2.34 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural yield strength | 23.0 °C | 86 MPa Show Material materials with Flexural yield strength of 86 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 534 J/m Show Material materials with Impact strength, Izod notched, ASTM of 534 J/m | ASTM D 256 |
23.0 °C | 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 | |
Yield strength | 23.0 °C | 56 MPa Show Material materials with Yield strength of 56 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 110 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 110 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ASTM C177 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 9 g/10min Show Material materials with Melt mass-flow rate of 9 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Audio,Auto Aftermarket,Circuit Protection,Cluster,Console,Data Management,Data Transfer,Displays,Document Handling,Door Handle,Doors Hardware/Trim,Electronic Components,Enclosure/Housing/Cover,Enclosures,Exterior Trim,Exterior,Forward Lighting,Front Grille,Glove Box,Headliner,Heavy Vehicles,HVAC Underhood,Infotainment/Telematic,Interior,LED Lighting,Non-LED Lighting,Overhead,Personal Computing,Recreational Vehicle,Refrigerator,Seat,Spoiler,Structure,Trim,Wheel Cover,Wiring Devices | |
| Processing methods | Drying Temperature: 105-110°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 275-300°C, Nozzle Temperature: 275-300°C, Front - Zone 3 Temperature: 260-300°C, Middle - Zone 2 Temperature: 255-295°C, Rear - Zone 1 Temperature: 250-290°C, Mold Temperature: 60-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm | |