General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.13 g/cm³ Show Material materials with Density of 1.13 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.1 % Show Material materials with Water absorption of 0.1 % | ASTM D 570 | 24 Hours |
Water absorption, equilibrium | 23.0 °C | 0.4 % Show Material materials with Water absorption, equilibrium of 0.4 % | ASTM D 570 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.06 GPa Show Material materials with Elastic modulus of 2.06 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 100 % Show Material materials with Elongation of 100 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.06 GPa Show Material materials with Flexural modulus of 2.06 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural yield strength | 23.0 °C | 77 MPa Show Material materials with Flexural yield strength of 77 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 427 J/m Show Material materials with Impact strength, Izod notched, ASTM of 427 J/m | ASTM D 256 |
23.0 °C | 534 J/m Show Material materials with Impact strength, Izod notched, ASTM of 534 J/m | ASTM D 256 | |
Yield strength | 23.0 °C | 52 MPa Show Material materials with Yield strength of 52 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 8.1E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 104 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 104 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Melting point | 245 - 260 °C Show Material materials with Melting point of 245 - 260 °C | ||
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ASTM C177 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Shrinkage | 23.0 °C | 0.4 - 0.7 % Show Material materials with Shrinkage of 0.4 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosures | |
Processing methods | Drying Temperature: 100-110°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 24hrs, Maximum Moisture Content: 0.04-0.05%, Minimum Moisture Content: 0.04%, Barrel - Zone 1 Temperature: 240-250°C, Barrel - Zone 2 Temperature: 240-255°C, Barrel - Zone 3 Temperature: 240-255°C, Barrel - Zone 4 Temperature: 240-255°C, Adapter - Zone 5 Temperature: 245-260°C, Head - Zone 6 - Top Temperature: 245-260°C, Head - Zone 7 - Bottom Temperature: 245-260°C, Screw Speed: 20-50rpm, Extruder Feed Zone Temperature: 60-80°C, Mold Temperature: 40-90°C, Die Temperature: 250-265°C |