CYCOLOY™ Resin MC8800

Want to keep this datasheet? Save it now in your required format

Description

PC/ABS, high heat, high impact, low CTE.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.22 g/cm³

Show Material materials with Density of 1.22 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.1 %

Show Material materials with Water absorption of 0.1 %

ASTM D 570 | 24 Hours

Water absorption, equilibrium

23.0 °C

0.4 %

Show Material materials with Water absorption, equilibrium of 0.4 %

ASTM D 570

Mechanical

PropertyTemperatureValueComment

Elongation

23.0 °C

120 %

Show Material materials with Elongation of 120 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

9 %

Show Material materials with Elongation at yield of 9 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

2.96 GPa

Show Material materials with Flexural modulus of 2.96 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural yield strength

23.0 °C

96 MPa

Show Material materials with Flexural yield strength of 96 MPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Impact strength, Izod notched, ASTM

-30.0 °C

106 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 106 J/m

ASTM D 256

23.0 °C

427 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 427 J/m

ASTM D 256

Tensile strength

23.0 °C

58 MPa

Show Material materials with Tensile strength of 58 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

55 MPa

Show Material materials with Yield strength of 55 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

6.66E-5 1/K

Show Material materials with Coefficient of thermal expansion of 6.66E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

8.1E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 8.1E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

126 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 126 °C

ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed

Thermal conductivity

23.0 °C

0.2 W/(m·K)

Show Material materials with Thermal conductivity of 0.2 W/(m·K)

ASTM C177

Vicat softening temperature

117 °C

Show Material materials with Vicat softening temperature of 117 °C

ASTM D 1525 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

10 g/10min

Show Material materials with Melt mass-flow rate of 10 g/10min

ASTM D 1238 | 260°C/5.0 kgf

Shrinkage

23.0 °C

0.4 - 0.6 %

Show Material materials with Shrinkage of 0.4 - 0.6 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Applique,Auto Aftermarket,Personal Computing,Trim,Wireless Communications

Processing methods

Drying Temperature: 110-120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-300°C, Front - Zone 3 Temperature: 270-300°C, Middle - Zone 2 Temperature: 265-290°C, Rear - Zone 1 Temperature: 260-270°C, Mold Temperature: 75-100°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm