General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.04 g/cm³ Show Material materials with Density of 1.04 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.27 GPa Show Material materials with Elastic modulus of 2.27 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 24 % Show Material materials with Elongation of 24 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 2.34 GPa Show Material materials with Flexural modulus of 2.34 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Flexural yield strength | 23.0 °C | 72 MPa Show Material materials with Flexural yield strength of 72 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 320 J/m Show Material materials with Impact strength, Izod notched, ASTM of 320 J/m | ASTM D 256 |
Tensile strength | 23.0 °C | 34 MPa Show Material materials with Tensile strength of 34 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 44 MPa Show Material materials with Yield strength of 44 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.82E-5 1/K Show Material materials with Coefficient of thermal expansion of 8.82E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.82E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.82E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Vicat softening temperature | 99 °C Show Material materials with Vicat softening temperature of 99 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94HB Flame Class Rating | 1.52mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 0 V Show Material materials with Comparative tracking index of 0 V | UL 746A |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 18 g/10min Show Material materials with Melt mass-flow rate of 18 g/10min | ISO 1133 | 220°C/10.0 kg | |
Melt viscosity | 23.0 °C | 225 Pa·s Show Material materials with Melt viscosity of 225 Pa·s | ASTM D 3825 | 240°C, 1000 sec⁻¹ |
Shrinkage | 23.0 °C | 0.5 - 0.8 % Show Material materials with Shrinkage of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosures,Fixture Bath/Shower,Food Processor,Non-LED Lighting,Sanitary,Swimming Pool/Spa,Water Treatment/Filtration | |
Processing methods | Drying Temperature: 80-95°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 220-260°C, Nozzle Temperature: 220-260°C, Front - Zone 3 Temperature: 215-240°C, Middle - Zone 2 Temperature: 205-225°C, Rear - Zone 1 Temperature: 190-210°C, Mold Temperature: 50-70°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm |