General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.04 g/cm³ Show Material materials with Density of 1.04 g/cm³ | ASTM D 792 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 2.5 GPa Show Material materials with Elastic modulus of 2.5 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 20 % Show Material materials with Elongation of 20 % | ISO 527 | 50 mm/min |
Elongation at yield | 23.0 °C | 2.4 % Show Material materials with Elongation at yield of 2.4 % | ISO 527 | 50 mm/min |
Flexural modulus | 23.0 °C | 2.25 GPa Show Material materials with Flexural modulus of 2.25 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 68 MPa Show Material materials with Flexural yield strength of 68 MPa | ISO 178 | 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 112 [-] Show Material materials with Hardness, Rockwell R of 112 [-] | ASTM D 785 |
Impact strength, Izod notched | -30.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A |
23.0 °C | 20 kJ/m² Show Material materials with Impact strength, Izod notched of 20 kJ/m² | ISO 180/1A | |
Tensile strength | 23.0 °C | 33 MPa Show Material materials with Tensile strength of 33 MPa | ISO 527 | 50 mm/min |
Yield strength | 23.0 °C | 45 MPa Show Material materials with Yield strength of 45 MPa | ISO 527 | 50 mm/min |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.82E-5 1/K Show Material materials with Coefficient of thermal expansion of 8.82E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 8.82E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.82E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Vicat softening temperature | 99 °C Show Material materials with Vicat softening temperature of 99 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 17 g/10min Show Material materials with Melt mass-flow rate of 17 g/10min | ISO 1133 | 220°C/10.0 kg | |
Melt viscosity | 23.0 °C | 225 Pa·s Show Material materials with Melt viscosity of 225 Pa·s | ASTM D 3825 | 240°C, 1000 sec⁻¹ |
Shrinkage | 23.0 °C | 0.5 - 0.8 % Show Material materials with Shrinkage of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Doors Hardware/Trim,Electronic Components,Exterior,Front Grille,Glove Box,Non-LED Lighting,Small Appliance,Trim,Washing Machine,Window,Wiring Devices | |
| Processing methods | Drying Temperature: 80-95°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 220-260°C, Nozzle Temperature: 220-260°C, Front - Zone 3 Temperature: 215-240°C, Middle - Zone 2 Temperature: 205-225°C, Rear - Zone 1 Temperature: 190-210°C, Mold Temperature: 50-70°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm | |