Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.22 g/cm³ Show Material materials with Density of 1.22 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.17 % Show Material materials with Water absorption of 0.17 % | ISO 62 | 23°C, 50% RH |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 2.5 GPa Show Material materials with Elastic modulus of 2.5 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 93 % Show Material materials with Elongation of 93 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5.6 % Show Material materials with Elongation at yield of 5.6 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.43 GPa Show Material materials with Flexural modulus of 2.43 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | -30.0 °C | 16 kJ/m² Show Material materials with Impact strength, Charpy notched of 16 kJ/m² | ISO 179/1eA |
23.0 °C | 62 kJ/m² Show Material materials with Impact strength, Charpy notched of 62 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -30.0 °C | 132 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 132 kJ/m² | ISO 179/1eU |
23.0 °C | 133 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 133 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 15 kJ/m² Show Material materials with Impact strength, Izod notched of 15 kJ/m² | ISO 180/1A |
23.0 °C | 63 kJ/m² Show Material materials with Impact strength, Izod notched of 63 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 130 J/m Show Material materials with Impact strength, Izod notched, ASTM of 130 J/m | ASTM D 256 |
23.0 °C | 760 J/m Show Material materials with Impact strength, Izod notched, ASTM of 760 J/m | ASTM D 256 | |
Impact strength, Izod unnotched | -30.0 °C | 180 kJ/m² Show Material materials with Impact strength, Izod unnotched of 180 kJ/m² | ISO 180/1U |
23.0 °C | 181 kJ/m² Show Material materials with Impact strength, Izod unnotched of 181 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched, ASTM | -30.0 °C | 2100 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 2100 J/m | ASTM D 4812 |
23.0 °C | 2150 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 2150 J/m | ASTM D 4812 | |
Tensile strength | 23.0 °C | 59 MPa Show Material materials with Tensile strength of 59 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 60 MPa Show Material materials with Yield strength of 60 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 6.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6.8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 119 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 119 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Relative temperature index, electrical | 125 °C Show Material materials with Relative temperature index, electrical of 125 °C | UL 746B | |||
Relative temperature index, mechanical impact | 110 °C Show Material materials with Relative temperature index, mechanical impact of 110 °C | UL 746B | |||
Relative temperature index, mechanical strength | 120 °C Show Material materials with Relative temperature index, mechanical strength of 120 °C | UL 746B | |||
Vicat softening temperature | 138 °C Show Material materials with Vicat softening temperature of 138 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94-5VB Flame Class Rating | 1.8mm | UL 94 | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+17 - 1.00E+18 Ω·cm Show Material materials with Volume resistivity of 1.00E+17 - 1.00E+18 Ω·cm | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 22 g/10min Show Material materials with Melt mass-flow rate of 22 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Melt volume-flow rate | 21 cm³/10min Show Material materials with Melt volume-flow rate of 21 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.6 - 0.8 % Show Material materials with Shrinkage of 0.6 - 0.8 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.6 - 0.8 % Show Material materials with Shrinkage, transverse of 0.6 - 0.8 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Data Transfer,Displays,Document Handling,Electronic Components,Enclosures,LED Lighting,Personal Computing,Security/Detection,Wireless Communications,Wiring Devices | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-310°C, Nozzle Temperature: 280-305°C, Front - Zone 3 Temperature: 290-310°C, Middle - Zone 2 Temperature: 275-300°C, Rear - Zone 1 Temperature: 265-290°C, Mold Temperature: 70-95°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm | |