General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Material materials with Density of 1.19 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.15 % Show Material materials with Water absorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.27 GPa Show Material materials with Elastic modulus of 2.27 GPa | ASTM D 638 | 50 mm/min | ||
Elongation | 23.0 °C | 125 % Show Material materials with Elongation of 125 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 6.3 % Show Material materials with Elongation at yield of 6.3 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.2 GPa Show Material materials with Flexural modulus of 2.2 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 94 MPa Show Material materials with Flexural yield strength of 94 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Charpy notched | -30.0 °C | 15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/1eA | ||
23.0 °C | 75 kJ/m² Show Material materials with Impact strength, Charpy notched of 75 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -30.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 70 kJ/m² Show Material materials with Impact strength, Izod notched of 70 kJ/m² | ISO 180/1A | |||
Impact strength, Izod notched, ASTM | -30.0 °C | 14 J/m Show Material materials with Impact strength, Izod notched, ASTM of 14 J/m | ASTM D 256 | ||
23.0 °C | 918 J/m Show Material materials with Impact strength, Izod notched, ASTM of 918 J/m | ASTM D 256 | |||
Tensile strength | 23.0 °C | 72 MPa Show Material materials with Tensile strength of 72 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Yield strength | 23.0 °C | 62 MPa Show Material materials with Yield strength of 62 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Charpy unnotched | No Break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No Break @ 23,-30°C| ISO 180/1U |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.74E-5 1/K Show Material materials with Coefficient of thermal expansion of 7.74E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7.74E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7.74E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 129 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Vicat softening temperature | 150 °C Show Material materials with Vicat softening temperature of 150 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 7.4 g/10min Show Material materials with Melt mass-flow rate of 7.4 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Melt volume-flow rate | 6 cm³/10min Show Material materials with Melt volume-flow rate of 6 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.6 - 0.8 % Show Material materials with Shrinkage of 0.6 - 0.8 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage, transverse of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Data Management,Personal Care | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 48hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 310-330°C, Nozzle Temperature: 305-325°C, Front - Zone 3 Temperature: 310-330°C, Middle - Zone 2 Temperature: 300-320°C, Rear - Zone 1 Temperature: 290-310°C, Mold Temperature: 80-115°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 40-60%, Vent Depth: 0.025-0.076mm |