SABIC® HDPE P6006NA

Want to keep this datasheet? Save it now in your required format

Description

P6006NA is a high density Polyethylene (potentially ASTM PE4710 cell class requirements) with multimodal distribution of the molecular mass. This is natural color grade suitable for pipe extrusion with excellent combination of properties. It is also suitable for use in telecommunication ducting, corrugated pipes and spiral pipes.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

0.95 g/cm³

Show Material materials with Density of 0.95 g/cm³

ASTM D1505

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

0.85 GPa

Show Material materials with Elastic modulus of 0.85 GPa

ASTM D638

Elongation at yield

23.0 °C

10 %

Show Material materials with Elongation at yield of 10 %

ISO 527-1/-2

Hardness, Shore D

23.0 °C

63 [-]

Show Material materials with Hardness, Shore D of 63 [-]

ASTM D2240

Impact strength, Charpy notched

23.0 °C

25 kJ/m²

Show Material materials with Impact strength, Charpy notched of 25 kJ/m²

ISO 179

Yield strength

23.0 °C

23 MPa

Show Material materials with Yield strength of 23 MPa

ASTM D638

Thermal

PropertyValueComment

Vicat softening temperature

74 °C

Show Material materials with Vicat softening temperature of 74 °C

ISO 306 | 50N (VST/B)

Technological properties

Property
Application areas

Telecommunication ducting, corrugated pipes and spiral pipes.