General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.2 g/cm³ Show Material materials with Density of 1.2 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.35 % Show Material materials with Water absorption of 0.35 % | ISO 62 |
Water absorption, equilibrium | 23.0 °C | 0.35 % Show Material materials with Water absorption, equilibrium of 0.35 % | ASTM D 570 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.35 GPa Show Material materials with Elastic modulus of 2.35 GPa | ASTM D 638 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.3 GPa Show Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ASTM D 785 | ||
Impact strength, Izod notched | -30.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 70 kJ/m² Show Material materials with Impact strength, Izod notched of 70 kJ/m² | ISO 180/1A | |||
Impact strength, Izod notched, ASTM | 23.0 °C | 700 J/m Show Material materials with Impact strength, Izod notched, ASTM of 700 J/m | ASTM D 256 | ||
Yield strength | 23.0 °C | 63 MPa Show Material materials with Yield strength of 63 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Izod unnotched | No Break @ 23,-30°C| ISO 180/1U | ||||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion of 7E-5 1/K | ASTM E 831 | -40°C to 95°C | ||
Heat deflection temperature, 0.45 MPa | 135 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75/Bf | 0.45 MPa | |||
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 141 °C Show Material materials with Vicat softening temperature of 141 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94V-2 Flame Class Rating | 1.5mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 3 [-] Show Material materials with Dielectric constant of 3 [-] | ASTM D 150 | at 1 MHz |
Dielectric strength | 23.0 °C | 27 kV/mm Show Material materials with Dielectric strength of 27 kV/mm | ASTM D 149 | 1.6 mm |
Dissipation factor | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor of 0.01 [-] | ASTM D 150 | at 1 MHz |
Optical
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 18 g/10min Show Material materials with Melt mass-flow rate of 18 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Melt volume-flow rate | 17 cm³/10min Show Material materials with Melt volume-flow rate of 17 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 280-300°C, Nozzle Temperature: 270-290°C, Front - Zone 3 Temperature: 280-300°C, Middle - Zone 2 Temperature: 270-290°C, Rear - Zone 1 Temperature: 260-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-100°C |