VALOX™ Resin SHF4330

Want to keep this datasheet? Save it now in your required format

Description

15% GF reinforced PBT/ASA, High Flow version

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.39 g/cm³

Show Material materials with Density of 1.39 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

5.3 GPa

Show Material materials with Elastic modulus of 5.3 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

3 %

Show Material materials with Elongation of 3 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

3 %

Show Material materials with Elongation at yield of 3 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

4.8 GPa

Show Material materials with Flexural modulus of 4.8 GPa

ISO 178 | 2 mm/min

Flexural strain

23.0 °C

3 %

Show Material materials with Flexural strain of 3 %

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

120 MPa

Show Material materials with Flexural strength of 120 MPa

ISO 178

Flexural yield strength

23.0 °C

120 MPa

Show Material materials with Flexural yield strength of 120 MPa

ISO 178 | 2 mm/min

Hardness, Ball Indentation

23.0 °C

160 MPa

Show Material materials with Hardness, Ball Indentation of 160 MPa

ISO 2039-1

Hardness, Rockwell R

23.0 °C

120 [-]

Show Material materials with Hardness, Rockwell R of 120 [-]

ISO 2039-2

Impact strength, Charpy notched

-30.0 °C

4 kJ/m²

Show Material materials with Impact strength, Charpy notched of 4 kJ/m²

ISO 179/2C

23.0 °C

4 kJ/m²

Show Material materials with Impact strength, Charpy notched of 4 kJ/m²

ISO 179/2C

Impact strength, Charpy unnotched

-30.0 °C

20 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 20 kJ/m²

ISO 179/2C

23.0 °C

30 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 30 kJ/m²

ISO 179/2C

Unlock all property charts

Impact strength, Izod notched

-30.0 °C

4 kJ/m²

Show Material materials with Impact strength, Izod notched of 4 kJ/m²

ISO 180/1A

23.0 °C

4 kJ/m²

Show Material materials with Impact strength, Izod notched of 4 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod unnotched

-30.0 °C

20 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 20 kJ/m²

ISO 180/1U

23.0 °C

28 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 28 kJ/m²

ISO 180/1U

Unlock all property charts

Tensile strength

23.0 °C

85 MPa

Show Material materials with Tensile strength of 85 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

85 MPa

Show Material materials with Yield strength of 85 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyValueComment

Heat deflection temperature, 0.45 MPa

204 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 204 °C

ISO 75/Bf | 0.45 MPa

Vicat softening temperature

159 °C

Show Material materials with Vicat softening temperature of 159 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt viscosity

260.0 °C

90 Pa·s

Show Material materials with Melt viscosity of 90 Pa·s

ISO 11443 | 1500 sec⁻¹

Melt volume-flow rate

40 cm³/10min

Show Material materials with Melt volume-flow rate of 40 cm³/10min

ISO 1133 | 250°C/5.0 kg

Shrinkage

23.0 °C

0.2 - 0.6 %

Show Material materials with Shrinkage of 0.2 - 0.6 %

SABIC method

Technological properties

Property
Application areas

Automotive

Fillers

15% Glass Fiber

Processing methods

Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C