Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.53 g/cm³ Show Material materials with Density of 1.53 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.06 % Show Material materials with Water absorption of 0.06 % | ISO 62 | 23°C, 50% RH |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 11.9 GPa Show Material materials with Elastic modulus of 11.9 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 7.72 GPa Show Material materials with Flexural modulus of 7.72 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 165 MPa Show Material materials with Flexural yield strength of 165 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 95 J/m Show Material materials with Impact strength, Izod notched, ASTM of 95 J/m | ASTM D 256 |
23.0 °C | 92 J/m Show Material materials with Impact strength, Izod notched, ASTM of 92 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 111 MPa Show Material materials with Tensile strength of 111 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 111 MPa Show Material materials with Yield strength of 111 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1E-4 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 3E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 3E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 214 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 214 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Vicat softening temperature | 200 °C Show Material materials with Vicat softening temperature of 200 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt mass-flow rate | 30 g/10min Show Material materials with Melt mass-flow rate of 30 g/10min | ASTM D 1238 | 250°C/2.16 kg | |
Melt volume-flow rate | 30 cm³/10min Show Material materials with Melt volume-flow rate of 30 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.3 - 0.5 % Show Material materials with Shrinkage of 0.3 - 0.5 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Data Transfer | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |