General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.29 g/cm³ Show Material materials with Density of 1.29 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.08 % Show Material materials with Water absorption of 0.08 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.5 GPa Show Material materials with Elastic modulus of 2.5 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 160 % Show Material materials with Elongation of 160 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 3.7 % Show Material materials with Elongation at yield of 3.7 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.2 GPa Show Material materials with Flexural modulus of 2.2 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 75 MPa Show Material materials with Flexural yield strength of 75 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 2 kJ/m² Show Material materials with Impact strength, Izod notched of 2 kJ/m² | ISO 180/1A |
23.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 25 J/m Show Material materials with Impact strength, Izod notched, ASTM of 25 J/m | ASTM D 256 |
23.0 °C | 59 J/m Show Material materials with Impact strength, Izod notched, ASTM of 59 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 31 MPa Show Material materials with Tensile strength of 31 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 48 MPa Show Material materials with Yield strength of 48 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 9.18E-5 1/K Show Material materials with Coefficient of thermal expansion of 9.18E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.9E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7.9E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 47 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 47 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Vicat softening temperature | 156 °C Show Material materials with Vicat softening temperature of 156 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Recognized, 94HB Flame Class Rating | 1.5mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 2.9 [-] Show Material materials with Dielectric constant of 2.9 [-] | ASTM D 150 | at 1 MHz |
Dielectric strength | 23.0 °C | 15.9 kV/mm Show Material materials with Dielectric strength of 15.9 kV/mm | ASTM D 149 | in air, 0.8 mm |
Dissipation factor | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor of 0.02 [-] | ASTM D 150 | at 1 MHz |
Electrical resistivity | 23.0 °C | 1.00E+15 Ω·m Show Material materials with Electrical resistivity of 1.00E+15 Ω·m | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 17 g/10min Show Material materials with Melt mass-flow rate of 17 g/10min | ASTM D 1238 | 250°C/1.2 kgf | |
Melt volume-flow rate | 16 cm³/10min Show Material materials with Melt volume-flow rate of 16 cm³/10min | ISO 1133 | 250°C/1.2 kg | |
Shrinkage | 23.0 °C | 2.1 - 2.3 % Show Material materials with Shrinkage of 2.1 - 2.3 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 2.1 - 2.3 % Show Material materials with Shrinkage, transverse of 2.1 - 2.3 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Medical Device,Wireless Communications, hinge applications. | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 50-75°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm |