VALOX™ Resin VIC4311

Want to keep this datasheet? Save it now in your required format

Description

VALOX VIC4311 is a 30% glass filled, impact modified PBT with excellent epoxy adhesion. Automotive underhood applications such as ignition coil housings.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.42 g/cm³ Show Material materials with Density of 1.42 g/cm³	ASTM D 792
Water absorption	23.0 °C	0.07 % Show Material materials with Water absorption of 0.07 %	ASTM D 570 \| 24 Hours

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	5 % Show Material materials with Elongation of 5 %	SABIC - Japan Method
Flexural modulus	23.0 °C	6.08 GPa Show Material materials with Flexural modulus of 6.08 GPa	ASTM D 790
Flexural strength	23.0 °C	128 MPa Show Material materials with Flexural strength of 128 MPa	ASTM D 790
Impact strength, Izod notched, ASTM	23.0 °C	137 J/m Show Material materials with Impact strength, Izod notched, ASTM of 137 J/m	ASTM D 256
Yield strength	23.0 °C	96 MPa Show Material materials with Yield strength of 96 MPa	SABIC - Japan Method

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	3E-5 1/K Show Material materials with Coefficient of thermal expansion of 3E-5 1/K	TMA \| -30°C to 30°C
Heat deflection temperature, 1.80 MPa		205 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 205 °C	ASTM D 648 \| 1.82 MPa, 3.2mm, unannealed

Electrical

Property	Temperature	Value	Comment
Dielectric constant	23.0 °C	3 [-] Show Material materials with Dielectric constant of 3 [-]	ASTM D 150 \| at 50/60 Hz
Volume resistivity	23.0 °C	1.00E+18 Ω·cm Show Material materials with Volume resistivity of 1.00E+18 Ω·cm	ASTM D 257

Rheological Properties

Property	Temperature	Value	Comment
Shrinkage	23.0 °C	0.6 - 0.8 % Show Material materials with Shrinkage of 0.6 - 0.8 %	SABIC method \| 6.4 mm

Technological properties

Property
Application areas	Auto Aftermarket,Data Transfer,Electronic Components,Enclosures,EV Infrastructure
Fillers	30% Glass Fiber

VALOX™ Resin VIC4311