VALOX™ Resin VX3101N

Want to keep this datasheet? Save it now in your required format

Description

VALOX VX3101N is an unreinforced PBT injection moulding resin, with excellent flow properties, good hydrolitical stability and chemical resistance.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.31 g/cm³

Show Material materials with Density of 1.31 g/cm³

ISO 1183

Water absorption

23.0 °C

0.08 %

Show Material materials with Water absorption of 0.08 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.8 GPa

Show Material materials with Elastic modulus of 2.8 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

15 %

Show Material materials with Elongation of 15 %

ISO 527 | 50 mm/min

Elongation at yield

23.0 °C

3.5 %

Show Material materials with Elongation at yield of 3.5 %

ISO 527 | 50 mm/min

Flexural modulus

23.0 °C

2.6 GPa

Show Material materials with Flexural modulus of 2.6 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

85 MPa

Show Material materials with Flexural yield strength of 85 MPa

ISO 178 | 2 mm/min

Hardness, Ball Indentation

23.0 °C

100 MPa

Show Material materials with Hardness, Ball Indentation of 100 MPa

ISO 2039-1

Impact strength, Charpy notched

-30.0 °C

3 kJ/m²

Show Material materials with Impact strength, Charpy notched of 3 kJ/m²

ISO 179/1eA

23.0 °C

5 kJ/m²

Show Material materials with Impact strength, Charpy notched of 5 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

2 kJ/m²

Show Material materials with Impact strength, Izod notched of 2 kJ/m²

ISO 180/1A

23.0 °C

2 - 4 kJ/m²

Show Material materials with Impact strength, Izod notched of 2 - 4 kJ/m²

ISO 180/1A

Unlock all property charts

Tensile strength

23.0 °C

50 MPa

Show Material materials with Tensile strength of 50 MPa

ISO 527 | 50 mm/min

Yield strength

23.0 °C

65 MPa

Show Material materials with Yield strength of 65 MPa

ISO 527 | 50 mm/min

Impact strength, Charpy unnotched

No break @ 23,-30°C | ISO 179/1eU

Impact strength, Izod unnotched

No break @ 23,-30°C | ISO 180/1U

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.3E-4 1/K

Show Material materials with Coefficient of thermal expansion of 1.3E-4 1/K

ISO 11359-2 | 23°C to 60°C

Coefficient of thermal expansion, transverse

23.0 °C

1.3E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K

ISO 11359-2 | 23°C to 60°C

Heat deflection temperature, 1.80 MPa

60 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C

ISO 75/Ae | 1.8 MPa

Vicat softening temperature

185 °C

Show Material materials with Vicat softening temperature of 185 °C

ISO 306 | Rate B/120

Flammability

UL Compliant, 94HB Flame Class Rating | 1.5mm | UL 94 by SABIC-IP

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Material materials with Comparative tracking index of 600 V

IEC 60112

Dielectric constant

23.0 °C

3.1 [-]

Show Material materials with Dielectric constant of 3.1 [-]

IEC 60250 | at 50/60 Hz

Dielectric strength

23.0 °C

16 kV/mm

Show Material materials with Dielectric strength of 16 kV/mm

IEC 60243-1 | in oil, 3.2 mm

Dissipation factor

23.0 °C

0.02 [-]

Show Material materials with Dissipation factor of 0.02 [-]

IEC 60250 | at 1 MHz

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

20 cm³/10min

Show Material materials with Melt volume-flow rate of 20 cm³/10min

ISO 1133 | 250°C/1.2 kg

Shrinkage

23.0 °C

1.1 - 1.8 %

Show Material materials with Shrinkage of 1.1 - 1.8 %

SABIC method

Shrinkage, transverse

23.0 °C

0.9 - 1.8 %

Show Material materials with Shrinkage, transverse of 0.9 - 1.8 %

SABIC method

Technological properties

Property
Application areas

Electronic Components,Wiring Devices

Processing methods

Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C