VALOX™ Resin VX4910

Want to keep this datasheet? Save it now in your required format

Description

10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.3 g/cm³

Show Material materials with Density of 1.3 g/cm³

ASTM D 792

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.6 GPa

Show Material materials with Elastic modulus of 4.6 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

3 %

Show Material materials with Elongation of 3 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

3 %

Show Material materials with Elongation at yield of 3 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

3.8 GPa

Show Material materials with Flexural modulus of 3.8 GPa

ISO 178 | 2 mm/min

Flexural strain

23.0 °C

4 %

Show Material materials with Flexural strain of 4 %

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

115 MPa

Show Material materials with Flexural strength of 115 MPa

ISO 178

Flexural yield strength

23.0 °C

120 MPa

Show Material materials with Flexural yield strength of 120 MPa

ISO 178 | 2 mm/min

Hardness, Ball Indentation

23.0 °C

100 MPa

Show Material materials with Hardness, Ball Indentation of 100 MPa

ISO 2039-1

Hardness, Rockwell R

23.0 °C

120 [-]

Show Material materials with Hardness, Rockwell R of 120 [-]

ISO 2039-2

Impact strength, Charpy notched

-30.0 °C

5 kJ/m²

Show Material materials with Impact strength, Charpy notched of 5 kJ/m²

ISO 179/2C

23.0 °C

6 kJ/m²

Show Material materials with Impact strength, Charpy notched of 6 kJ/m²

ISO 179/2C

Impact strength, Charpy unnotched

-30.0 °C

20 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 20 kJ/m²

ISO 179/2C

23.0 °C

45 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m²

ISO 179/2C

Unlock all property charts

Impact strength, Izod notched

-30.0 °C

5 kJ/m²

Show Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A

23.0 °C

5 kJ/m²

Show Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-30.0 °C

45 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 45 J/m

ASTM D 256

23.0 °C

55 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 55 J/m

ASTM D 256

Unlock all property charts

Impact strength, Izod unnotched

-30.0 °C

25 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 25 kJ/m²

ISO 180/1U

23.0 °C

30 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 30 kJ/m²

ISO 180/1U

Unlock all property charts

Impact strength, Izod unnotched, ASTM

-30.0 °C

340 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 340 J/m

ASTM D 4812

23.0 °C

440 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 440 J/m

ASTM D 4812

Unlock all property charts

Tensile strength

23.0 °C

80 MPa

Show Material materials with Tensile strength of 80 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

80 MPa

Show Material materials with Yield strength of 80 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

3.57E-5 1/K

Show Material materials with Coefficient of thermal expansion of 3.57E-5 1/K

ISO 11359-2 | 23°C to 150°C

Coefficient of thermal expansion, transverse

23.0 °C

1.96E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.96E-4 1/K

ISO 11359-2 | 23°C to 150°C

Heat deflection temperature, 0.45 MPa

205 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 205 °C

ISO 75/Bf | 0.45 MPa

Vicat softening temperature

150 °C

Show Material materials with Vicat softening temperature of 150 °C

ASTM D 1525 | Rate B/50

Electrical

PropertyTemperatureValueComment

Dielectric constant

23.0 °C

3.4 [-]

Show Material materials with Dielectric constant of 3.4 [-]

ASTM D 150 | at 1 MHz

Dissipation factor

23.0 °C

0.02 [-]

Show Material materials with Dissipation factor of 0.02 [-]

ASTM D 150 | at 1 MHz

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

40 g/10min

Show Material materials with Melt mass-flow rate of 40 g/10min

ASTM D 1238 | 265°C/5.0 kgf

Melt viscosity

260.0 °C

160 Pa·s

Show Material materials with Melt viscosity of 160 Pa·s

ISO 11443 | 1500 sec⁻¹

Melt volume-flow rate

35 cm³/10min

Show Material materials with Melt volume-flow rate of 35 cm³/10min

ISO 1133 | 265°C/5.0 kg

Shrinkage

23.0 °C

0.6 - 0.8 %

Show Material materials with Shrinkage of 0.6 - 0.8 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Electronic Components,Monitoring and Imaging

Fillers

10% Glass Fiber

Processing methods

Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C