General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.31 g/cm³ Show Material materials with Density of 1.31 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.3 % Show Material materials with Water absorption of 0.3 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 5.6 GPa Show Material materials with Elastic modulus of 5.6 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 3 % Show Material materials with Elongation of 3 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 4.6 GPa Show Material materials with Flexural modulus of 4.6 GPa | ISO 178 | 2 mm/min |
Flexural strain | 23.0 °C | 4 % Show Material materials with Flexural strain of 4 % | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 130 MPa Show Material materials with Flexural strength of 130 MPa | ISO 178 |
Flexural yield strength | 23.0 °C | 130 MPa Show Material materials with Flexural yield strength of 130 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 100 MPa Show Material materials with Hardness, Ball Indentation of 100 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -30.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/2C |
23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/2C | |
Impact strength, Charpy unnotched | -30.0 °C | 30 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 30 kJ/m² | ISO 179/2C |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/2C | |
Impact strength, Izod notched | -30.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A |
23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 50 J/m Show Material materials with Impact strength, Izod notched, ASTM of 50 J/m | ASTM D 256 |
23.0 °C | 65 J/m Show Material materials with Impact strength, Izod notched, ASTM of 65 J/m | ASTM D 256 | |
Impact strength, Izod unnotched | -30.0 °C | 25 kJ/m² Show Material materials with Impact strength, Izod unnotched of 25 kJ/m² | ISO 180/1U |
23.0 °C | 35 kJ/m² Show Material materials with Impact strength, Izod unnotched of 35 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched, ASTM | -30.0 °C | 490 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 490 J/m | ASTM D 4812 |
23.0 °C | 520 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 520 J/m | ASTM D 4812 | |
Tensile strength | 23.0 °C | 85 MPa Show Material materials with Tensile strength of 85 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 85 MPa Show Material materials with Yield strength of 85 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.72E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.72E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.91E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.91E-4 1/K | ISO 11359-2 | 23°C to 150°C |
Heat deflection temperature, 0.45 MPa | 200 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 200 °C | ISO 75/Bf | 0.45 MPa | |
Vicat softening temperature | 135 °C Show Material materials with Vicat softening temperature of 135 °C | ASTM D 1525 | Rate B/50 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 575 V Show Material materials with Comparative tracking index of 575 V | IEC 60112 |
Dielectric constant | 23.0 °C | 3 [-] Show Material materials with Dielectric constant of 3 [-] | ASTM D 150 | at 1 MHz |
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor of 0.02 [-] | ASTM D 150 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 33 g/10min Show Material materials with Melt mass-flow rate of 33 g/10min | ASTM D 1238 | 265°C/5.0 kgf | |
Melt viscosity | 260.0 °C | 155 Pa·s Show Material materials with Melt viscosity of 155 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Melt volume-flow rate | 30 cm³/10min Show Material materials with Melt volume-flow rate of 30 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.2 - 0.6 % Show Material materials with Shrinkage of 0.2 - 0.6 % | SABIC method |
Shrinkage, transverse | 23.0 °C | 0.3 - 0.7 % Show Material materials with Shrinkage, transverse of 0.3 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Medical Device,Structure | |
Fillers | 15% Glass Fiber | |
Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C |