Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.04 g/cm³ Show Material materials with Density of 1.04 g/cm³ | ASTM D 792 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.37 GPa Show Material materials with Elastic modulus of 2.37 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 27 % Show Material materials with Elongation of 27 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 2.6 % Show Material materials with Elongation at yield of 2.6 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 2.17 GPa Show Material materials with Flexural modulus of 2.17 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 69 MPa Show Material materials with Flexural yield strength of 69 MPa | ISO 178 | 2 mm/min |
Hardness, Rockwell R | 23.0 °C | 104 [-] Show Material materials with Hardness, Rockwell R of 104 [-] | ASTM D 785 |
Impact strength, Charpy notched | -30.0 °C | 11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/1eA |
23.0 °C | 25 kJ/m² Show Material materials with Impact strength, Charpy notched of 25 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -40.0 °C | 9 kJ/m² Show Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A |
-30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod notched of 10 kJ/m² | ISO 180/1A | |
23.0 °C | 25 kJ/m² Show Material materials with Impact strength, Izod notched of 25 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | 23.0 °C | 240 - 300 J/m Show Material materials with Impact strength, Izod notched, ASTM of 240 - 300 J/m | ASTM D 256 |
Tensile strength | 23.0 °C | 33 MPa Show Material materials with Tensile strength of 33 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 42 MPa Show Material materials with Yield strength of 42 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 93 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 93 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |
Vicat softening temperature | 106 °C Show Material materials with Vicat softening temperature of 106 °C | ISO 306 | Rate B/120 | |
Flammability | UL Recognized, 94HB Flame Class Rating | 1.5mm | UL 94 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 10 g/10min Show Material materials with Melt mass-flow rate of 10 g/10min | ISO 1133 | 220°C/10.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.8 % Show Material materials with Shrinkage of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Air Cabin Interiors,Applique,Auto Aftermarket,Cladding,Cluster,Console,Cowl Vent Grille,Doors Hardware/Trim,Electronic Components,Enclosures,Exterior Mirror,Exterior Trim,Food Processor,Front Grille,Glove Box,Infotainment/Telematic,Interior,Overhead,Rear/Signal Lighting,Recreational Vehicle,Seat,Spoiler,Surgical Devices,Trim | |
Processing methods | Drying Temperature: 90-95°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.1%, Melt Temperature: 230-275°C, Nozzle Temperature: 230-275°C, Front - Zone 3 Temperature: 230-255°C, Middle - Zone 2 Temperature: 210-225°C, Rear - Zone 1 Temperature: 195-210°C, Mold Temperature: 50-80°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 30-60rpm, Shot to Cylinder Size: 50-70%, Vent Depth: 0.038-0.051mm |