XENOY™ Resin X2420

Want to keep this datasheet? Save it now in your required format

Description

XENOYX2420 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and impact strength. X2420 has enhanced melt flowability, impact ductility and broad color space.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.28 g/cm³

Show Material materials with Density of 1.28 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.04 %

Show Material materials with Water absorption of 0.04 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.8 GPa

Show Material materials with Elastic modulus of 3.8 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

7 %

Show Material materials with Elongation of 7 %

ISO 527 | 5 mm/min

Elongation at yield

23.0 °C

3 %

Show Material materials with Elongation at yield of 3 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

3.5 GPa

Show Material materials with Flexural modulus of 3.5 GPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Flexural yield strength

23.0 °C

90 MPa

Show Material materials with Flexural yield strength of 90 MPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Impact strength, Charpy notched

-30.0 °C

7 kJ/m²

Show Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/1eA

23.0 °C

15 kJ/m²

Show Material materials with Impact strength, Charpy notched of 15 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

-30.0 °C

95 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 95 kJ/m²

ISO 179/1eU

23.0 °C

95 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 95 kJ/m²

ISO 179/1eU

Unlock all property charts

Impact strength, Izod notched

-30.0 °C

8 kJ/m²

Show Material materials with Impact strength, Izod notched of 8 kJ/m²

ISO 180/1A

23.0 °C

14 kJ/m²

Show Material materials with Impact strength, Izod notched of 14 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

23.0 °C

205 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 205 J/m

ASTM D 256

Impact strength, Izod unnotched

-30.0 °C

74 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 74 kJ/m²

ISO 180/1U

23.0 °C

110 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 110 kJ/m²

ISO 180/1U

Unlock all property charts

Impact strength, Izod unnotched, ASTM

23.0 °C

1600 J/m

Show Material materials with Impact strength, Izod unnotched, ASTM of 1600 J/m

ASTM D 4812

Tensile strength

23.0 °C

35 MPa

Show Material materials with Tensile strength of 35 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

50 MPa

Show Material materials with Yield strength of 50 MPa

ASTM D 638 | Type I, 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5E-5 1/K

Show Material materials with Coefficient of thermal expansion of 5E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

8E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

101 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 101 °C

ASTM D 648 | 1.82 MPa, 3.2mm, unannealed

Relative temperature index, electrical

75 °C

Show Material materials with Relative temperature index, electrical of 75 °C

UL 746B

Relative temperature index, mechanical impact

75 °C

Show Material materials with Relative temperature index, mechanical impact of 75 °C

UL 746B

Relative temperature index, mechanical strength

75 °C

Show Material materials with Relative temperature index, mechanical strength of 75 °C

UL 746B

Vicat softening temperature

118 °C

Show Material materials with Vicat softening temperature of 118 °C

ISO 306 | Rate B/120

Flammability

UL Recognized, 94HB Flame Class Rating | 0.4mm | UL 94

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

26 cm³/10min

Show Material materials with Melt volume-flow rate of 26 cm³/10min

ISO 1133 | 300°C/1.2 kg

Shrinkage

23.0 °C

0.15 - 0.25 %

Show Material materials with Shrinkage of 0.15 - 0.25 %

SABIC method | 3.2 mm

Shrinkage, transverse

23.0 °C

0.3 - 0.4 %

Show Material materials with Shrinkage, transverse of 0.3 - 0.4 %

SABIC method

Technological properties

Property
Application areas

Wireless Communications

Processing methods

Drying Temperature: 95-105°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 260-290°C, Front - Zone 3 Temperature: 255-290°C, Middle - Zone 2 Temperature: 255-290°C, Rear - Zone 1 Temperature: 250-280°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm