Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.21 g/cm³ Show Material materials with Density of 1.21 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.2 % Show Material materials with Water absorption of 0.2 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.2 GPa Show Material materials with Elastic modulus of 2.2 GPa | ASTM D 638 | 50 mm/min | ||
Elongation | 23.0 °C | 80 % Show Material materials with Elongation of 80 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.15 GPa Show Material materials with Flexural modulus of 2.15 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 79 MPa Show Material materials with Flexural strength of 79 MPa | ASTM D 790 | ||
Flexural yield strength | 23.0 °C | 80 MPa Show Material materials with Flexural yield strength of 80 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 95 MPa Show Material materials with Hardness, Ball Indentation of 95 MPa | ISO 2039-1 | ||
Impact strength, Charpy notched | -30.0 °C | 30 kJ/m² Show Material materials with Impact strength, Charpy notched of 30 kJ/m² | ISO 179/1eA | ||
23.0 °C | 50 kJ/m² Show Material materials with Impact strength, Charpy notched of 50 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -40.0 °C | 15 kJ/m² Show Material materials with Impact strength, Izod notched of 15 kJ/m² | ISO 180/1A | ||
-30.0 °C | 25 kJ/m² Show Material materials with Impact strength, Izod notched of 25 kJ/m² | ISO 180/1A | |||
23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Izod notched of 40 kJ/m² | ISO 180/1A | |||
Impact strength, Izod notched, ASTM | -30.0 °C | 200 J/m Show Material materials with Impact strength, Izod notched, ASTM of 200 J/m | ASTM D 256 | ||
23.0 °C | 600 J/m Show Material materials with Impact strength, Izod notched, ASTM of 600 J/m | ASTM D 256 | |||
Tensile strength | 23.0 °C | 55 MPa Show Material materials with Tensile strength of 55 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Yield strength | 23.0 °C | 56 MPa Show Material materials with Yield strength of 56 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Impact strength, Charpy unnotched | No break @ -30°C | ISO 179/2C | ||||
Impact strength, Izod unnotched | No break @ -30°C | ISO 180/1U |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8E-5 1/K Show Material materials with Coefficient of thermal expansion of 8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 108 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 108 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Thermal conductivity | 23.0 °C | 0.18 W/(m·K) Show Material materials with Thermal conductivity of 0.18 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 135 °C Show Material materials with Vicat softening temperature of 135 °C | ASTM D 1525 | Rate B/50 | |||
Flammability | UL Compliant, 94HB Flame Class Rating | 1.5mm | UL 94 by SABIC-IP |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant | 23.0 °C | 3.3 [-] Show Material materials with Dielectric constant of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor of 0.02 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 9 g/10min Show Material materials with Melt mass-flow rate of 9 g/10min | ASTM D 1238 | 265°C/2.16kgf | |
Melt volume-flow rate | 4 cm³/10min Show Material materials with Melt volume-flow rate of 4 cm³/10min | ISO 1133 | 265°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.8 % Show Material materials with Shrinkage of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 - 0.8 % Show Material materials with Shrinkage, transverse of 0.5 - 0.8 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components,Enclosure/Housing/Cover,Enclosures,Exterior,Personal Care,Personal Computing,Spoiler,Wireless Communications,Wiring Devices | |
Processing methods | Drying Temperature: 110-120°C, Drying Time: 4-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 265-275°C, Nozzle Temperature: 260-275°C, Front - Zone 3 Temperature: 260-280°C, Middle - Zone 2 Temperature: 250-275°C, Rear - Zone 1 Temperature: 240-270°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-100°C |