XENOY™ Resin X4820

Want to keep this datasheet? Save it now in your required format

Description

XENOY X4820 is a high modulus PC/PBT Blend. This resin provides high chemical resistance, excellent impact, very low creep, low CTE, excellent fatigue and dimensional stability.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.25 g/cm³

Show Material materials with Density of 1.25 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.14 %

Show Material materials with Water absorption of 0.14 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.2 GPa

Show Material materials with Elastic modulus of 3.2 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

140 %

Show Material materials with Elongation of 140 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

4.2 %

Show Material materials with Elongation at yield of 4.2 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.85 GPa

Show Material materials with Flexural modulus of 2.85 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

87 MPa

Show Material materials with Flexural yield strength of 87 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

23.0 °C

60 kJ/m²

Show Material materials with Impact strength, Charpy notched of 60 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

15 kJ/m²

Show Material materials with Impact strength, Izod notched of 15 kJ/m²

ISO 180/1A

23.0 °C

55 kJ/m²

Show Material materials with Impact strength, Izod notched of 55 kJ/m²

ISO 180/1A

Impact strength, Izod notched, ASTM

-30.0 °C

150 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 150 J/m

ASTM D 256

23.0 °C

700 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 700 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

58 MPa

Show Material materials with Tensile strength of 58 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

57 MPa

Show Material materials with Yield strength of 57 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7.5E-5 1/K

Show Material materials with Coefficient of thermal expansion of 7.5E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

1.1E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

98 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 98 °C

ASTM D 648 | 1.82 MPa, 3.2mm, unannealed

Vicat softening temperature

130 °C

Show Material materials with Vicat softening temperature of 130 °C

ASTM D 1525 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

10 g/10min

Show Material materials with Melt mass-flow rate of 10 g/10min

ASTM D 1238 | 250°C/5.0 kgf

Melt volume-flow rate

12 cm³/10min

Show Material materials with Melt volume-flow rate of 12 cm³/10min

ISO 1133 | 265°C/5.0 kg

Shrinkage

23.0 °C

0.95 - 1.1 %

Show Material materials with Shrinkage of 0.95 - 1.1 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Enclosures,Exterior,Lawn/Garden,Personal Computing,Wireless Communications

Processing methods

Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-275°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 245-265°C, Rear - Zone 1 Temperature: 240-260°C, Mold Temperature: 40-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm