XENOY™ Resin X4850

Want to keep this datasheet? Save it now in your required format

Description

XENOY X4850 is a hydrostable, high modulus, high ductile PC/PBT blend. Furthermore, this resin provides high chemicalresistance, very low creep, low CTE, excellent fatique and high heat dimensional stability. The X4850 could be positioned for body panels, safety equipment,housings, doorhandles, spring-loaded applications, medical device enclosures, outdoor sports equipment.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.31 g/cm³

Show Material materials with Density of 1.31 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.14 %

Show Material materials with Water absorption of 0.14 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4 GPa

Show Material materials with Elastic modulus of 4 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

140 %

Show Material materials with Elongation of 140 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

3.8 %

Show Material materials with Elongation at yield of 3.8 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

3.5 GPa

Show Material materials with Flexural modulus of 3.5 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

94 MPa

Show Material materials with Flexural yield strength of 94 MPa

ISO 178 | 2 mm/min

Hardness, Ball Indentation

23.0 °C

105 MPa

Show Material materials with Hardness, Ball Indentation of 105 MPa

ISO 2039-1

Impact strength, Charpy notched

-30.0 °C

11 kJ/m²

Show Material materials with Impact strength, Charpy notched of 11 kJ/m²

ISO 179/1eA

23.0 °C

20 kJ/m²

Show Material materials with Impact strength, Charpy notched of 20 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

7 kJ/m²

Show Material materials with Impact strength, Izod notched of 7 kJ/m²

ISO 180/1A

23.0 °C

11 - 20 kJ/m²

Show Material materials with Impact strength, Izod notched of 11 - 20 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-30.0 °C

100 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 100 J/m

ASTM D 256

23.0 °C

180 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 180 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

60 MPa

Show Material materials with Tensile strength of 60 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

58 MPa

Show Material materials with Yield strength of 58 MPa

ASTM D 638 | Type I, 5 mm/min

Impact strength, Charpy unnotched

No break @ 23,-30°C | ISO 179/1eU

Impact strength, Izod unnotched

No break @ 23,-30°C | ISO 180/1U

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.2E-5 1/K

Show Material materials with Coefficient of thermal expansion of 5.2E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

7.5E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 7.5E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

121 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 121 °C

ISO 75/Bf | 0.45 MPa

Thermal conductivity

23.0 °C

0.2 W/(m·K)

Show Material materials with Thermal conductivity of 0.2 W/(m·K)

ISO 8302

Vicat softening temperature

134 °C

Show Material materials with Vicat softening temperature of 134 °C

ASTM D 1525 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

4.5 g/10min

Show Material materials with Melt mass-flow rate of 4.5 g/10min

ASTM D 1238 | 266°C/5.0 kg

Melt volume-flow rate

4 cm³/10min

Show Material materials with Melt volume-flow rate of 4 cm³/10min

ISO 1133 | 265°C/5.0 kg

Shrinkage

23.0 °C

0.7 - 0.9 %

Show Material materials with Shrinkage of 0.7 - 0.9 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Auto Aftermarket,Door Handle,Enclosures,Exterior Trim,Front Grille,Heavy Vehicles,Lawn/Garden,Skid Plate

Processing methods

Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-80°C