XENOY™ Resin X4870HH

Want to keep this datasheet? Save it now in your required format

Description

XENOY X4870HH is a high heat, very high modulus and ductile PC/PET blend. Furthermore this resin provides chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional stability. The X4870HH could be positioned for body panels, housings, medical device enclosures, outdoor sports equipment.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.34 g/cm³

Show Material materials with Density of 1.34 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.14 %

Show Material materials with Water absorption of 0.14 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

4.6 GPa

Show Material materials with Elastic modulus of 4.6 GPa

ASTM D 638 | 5 mm/min

Elongation

23.0 °C

60 %

Show Material materials with Elongation of 60 %

ASTM D 638 | Type I, 5 mm/min

Elongation at yield

23.0 °C

3.7 %

Show Material materials with Elongation at yield of 3.7 %

ASTM D 638 | Type I, 5 mm/min

Flexural modulus

23.0 °C

4 GPa

Show Material materials with Flexural modulus of 4 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

98 MPa

Show Material materials with Flexural yield strength of 98 MPa

ISO 178 | 2 mm/min

Hardness, Ball Indentation

23.0 °C

105 MPa

Show Material materials with Hardness, Ball Indentation of 105 MPa

ISO 2039-1

Impact strength, Charpy notched

-30.0 °C

7 kJ/m²

Show Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/1eA

23.0 °C

11 kJ/m²

Show Material materials with Impact strength, Charpy notched of 11 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

6 kJ/m²

Show Material materials with Impact strength, Izod notched of 6 kJ/m²

ISO 180/1A

23.0 °C

10 kJ/m²

Show Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-30.0 °C

70 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 70 J/m

ASTM D 256

23.0 °C

90 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 90 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

45 MPa

Show Material materials with Tensile strength of 45 MPa

ASTM D 638 | Type I, 5 mm/min

Yield strength

23.0 °C

61 MPa

Show Material materials with Yield strength of 61 MPa

ASTM D 638 | Type I, 5 mm/min

Impact strength, Charpy unnotched

No break @ 23°C | ISO 179/2C

Impact strength, Izod unnotched

No break @ 23°C | ISO 180/1U

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

4.3E-5 1/K

Show Material materials with Coefficient of thermal expansion of 4.3E-5 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

6.4E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 6.4E-5 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 0.45 MPa

131 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 131 °C

ISO 75/Bf | 0.45 MPa

Thermal conductivity

23.0 °C

0.2 W/(m·K)

Show Material materials with Thermal conductivity of 0.2 W/(m·K)

ISO 8302

Vicat softening temperature

137 °C

Show Material materials with Vicat softening temperature of 137 °C

ASTM D 1525 | Rate B/50

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

8 g/10min

Show Material materials with Melt mass-flow rate of 8 g/10min

ASTM D 1238 | 266°C/5.0 kg

Melt volume-flow rate

7 cm³/10min

Show Material materials with Melt volume-flow rate of 7 cm³/10min

ISO 1133 | 265°C/5.0 kg

Shrinkage

23.0 °C

0.5 - 0.7 %

Show Material materials with Shrinkage of 0.5 - 0.7 %

SABIC method | 3.2 mm

Technological properties

Property
Application areas

Door Handle,Electronic Components,Enclosures,Food Processor,Wireless Communications

Processing methods

Drying Temperature: 110-120°C, Drying Time: 4-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 265-275°C, Nozzle Temperature: 260-275°C, Front - Zone 3 Temperature: 260-280°C, Middle - Zone 2 Temperature: 250-275°C, Rear - Zone 1 Temperature: 240-270°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-100°C