XENOY™ Resin X5100

Want to keep this datasheet? Save it now in your required format

Description

XENOY X5100 is a semi-crystalline, impact modified PC+PBT blend with excellent flow. (PC+PBT-I).

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.22 g/cm³

Show Material materials with Density of 1.22 g/cm³

ISO 1183

Water absorption

23.0 °C

0.15 %

Show Material materials with Water absorption of 0.15 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.15 GPa

Show Material materials with Elastic modulus of 2.15 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

50 %

Show Material materials with Elongation of 50 %

ISO 527 | 50 mm/min

Elongation at yield

23.0 °C

4.5 %

Show Material materials with Elongation at yield of 4.5 %

ISO 527 | 50 mm/min

Flexural modulus

23.0 °C

2.05 GPa

Show Material materials with Flexural modulus of 2.05 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

80 MPa

Show Material materials with Flexural yield strength of 80 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

-30.0 °C

15 kJ/m²

Show Material materials with Impact strength, Charpy notched of 15 kJ/m²

ISO 179/1eA

23.0 °C

50 kJ/m²

Show Material materials with Impact strength, Charpy notched of 50 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

18 kJ/m²

Show Material materials with Impact strength, Izod notched of 18 kJ/m²

ISO 180/1A

-20.0 °C

20 kJ/m²

Show Material materials with Impact strength, Izod notched of 20 kJ/m²

ISO 180/1A

-10.0 °C

35 kJ/m²

Show Material materials with Impact strength, Izod notched of 35 kJ/m²

ISO 180/1A

23.0 °C

40 - 45 kJ/m²

Show Material materials with Impact strength, Izod notched of 40 - 45 kJ/m²

ISO 180/1A

Unlock all property charts

Tensile strength

23.0 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

ISO 527 | 50 mm/min

Yield strength

23.0 °C

54 MPa

Show Material materials with Yield strength of 54 MPa

ISO 527 | 50 mm/min

Impact strength, Charpy unnotched

No break @ -30°C | ISO 179/2C

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

8.5E-5 1/K

Show Material materials with Coefficient of thermal expansion of 8.5E-5 1/K

ISO 11359-2 | -23°C to 80°C

Coefficient of thermal expansion, transverse

23.0 °C

8E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K

ISO 11359-2 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

84 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 84 °C

ISO 75/Ae | 1.8 MPa

Thermal conductivity

23.0 °C

0.2 W/(m·K)

Show Material materials with Thermal conductivity of 0.2 W/(m·K)

ISO 8302

Vicat softening temperature

120 °C

Show Material materials with Vicat softening temperature of 120 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt viscosity

260.0 °C

215 Pa·s

Show Material materials with Melt viscosity of 215 Pa·s

ISO 11443 | 1500 sec⁻¹

Melt volume-flow rate

13 cm³/10min

Show Material materials with Melt volume-flow rate of 13 cm³/10min

ISO 1133 | 250°C/2.16 kg

Shrinkage

23.0 °C

0.7 - 1 %

Show Material materials with Shrinkage of 0.7 - 1 %

SABIC method

Technological properties

Property
Application areas

Auto Aftermarket,Cluster,Enclosures,Exterior,Front Grille,Interior,Spoiler,Trim

Processing methods

Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-80°C