XENOY™ Resin X5230

Want to keep this datasheet? Save it now in your required format

Description

Mineral filled PC/PET blend with high flow, high heat, dimensional stability, low shrinkage and low CTE, especially for painted applications

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.33 g/cm³

Show Material materials with Density of 1.33 g/cm³

ISO 1183

Water absorption

23.0 °C

0.14 %

Show Material materials with Water absorption of 0.14 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

3.85 GPa

Show Material materials with Elastic modulus of 3.85 GPa

ISO 527 | 1 mm/min

Elongation

23.0 °C

9 %

Show Material materials with Elongation of 9 %

ISO 527 | 5 mm/min

Elongation at yield

23.0 °C

3.6 %

Show Material materials with Elongation at yield of 3.6 %

ISO 527 | 5 mm/min

Flexural modulus

23.0 °C

3.75 GPa

Show Material materials with Flexural modulus of 3.75 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

95 MPa

Show Material materials with Flexural yield strength of 95 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

23.0 °C

10 kJ/m²

Show Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

7 kJ/m²

Show Material materials with Impact strength, Izod notched of 7 kJ/m²

ISO 180/1A

23.0 °C

10 kJ/m²

Show Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A

Impact strength, Izod unnotched

-30.0 °C

120 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 120 kJ/m²

ISO 180/1U

23.0 °C

137 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 137 kJ/m²

ISO 180/1U

Unlock all property charts

Tensile strength

23.0 °C

42 MPa

Show Material materials with Tensile strength of 42 MPa

ISO 527 | 5 mm/min

Yield strength

23.0 °C

58 MPa

Show Material materials with Yield strength of 58 MPa

ISO 527 | 5 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

5.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 5.4E-5 1/K

ISO 11359-2 | -30°C to 80°C

Coefficient of thermal expansion, transverse

23.0 °C

7.4E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 7.4E-5 1/K

ISO 11359-2 | -30°C to 80°C

Heat deflection temperature, 1.80 MPa

109 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 109 °C

ISO 75/Af | 1.8 MPa

Vicat softening temperature

140 °C

Show Material materials with Vicat softening temperature of 140 °C

ISO 306 | Rate B/120

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

28 g/10min

Show Material materials with Melt mass-flow rate of 28 g/10min

ASTM D 1238 | 265°C/5.0 kgf

Melt volume-flow rate

24 cm³/10min

Show Material materials with Melt volume-flow rate of 24 cm³/10min

ISO 1133 | 265°C/5.0 kg

Shrinkage

23.0 °C

0.5 - 0.7 %

Show Material materials with Shrinkage of 0.5 - 0.7 %

SABIC method

Technological properties

Property
Application areas

Exterior Trim,Spoiler

Fillers

Mineral Powder

Processing methods

Drying Temperature: 110-120°C, Drying Time: 4-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 265-275°C, Nozzle Temperature: 260-275°C, Front - Zone 3 Temperature: 260-280°C, Middle - Zone 2 Temperature: 250-275°C, Rear - Zone 1 Temperature: 240-270°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-100°C