General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.23 g/cm³ Show Material materials with Density of 1.23 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.15 % Show Material materials with Water absorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.55 GPa Show Material materials with Elastic modulus of 2.55 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 110 % Show Material materials with Elongation of 110 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.18 GPa Show Material materials with Flexural modulus of 2.18 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 87 MPa Show Material materials with Flexural yield strength of 87 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy notched of 45 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 15 kJ/m² Show Material materials with Impact strength, Izod notched of 15 kJ/m² | ISO 180/1A |
23.0 °C | 50 kJ/m² Show Material materials with Impact strength, Izod notched of 50 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 180 J/m Show Material materials with Impact strength, Izod notched, ASTM of 180 J/m | ASTM D 256 |
23.0 °C | 747 J/m Show Material materials with Impact strength, Izod notched, ASTM of 747 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 51 MPa Show Material materials with Tensile strength of 51 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 62 MPa Show Material materials with Yield strength of 62 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7.02E-5 1/K Show Material materials with Coefficient of thermal expansion of 7.02E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7.56E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7.56E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 88 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 88 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Vicat softening temperature | 135 °C Show Material materials with Vicat softening temperature of 135 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 26 g/10min Show Material materials with Melt mass-flow rate of 26 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Melt volume-flow rate | 25 cm³/10min Show Material materials with Melt volume-flow rate of 25 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.7 - 0.9 % Show Material materials with Shrinkage of 0.7 - 0.9 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Building Accessory,Enclosure/Housing/Cover,Heavy Vehicles,Medical Device,Motorcycle,Non-LED Lighting,Personal Water Craft,Power Manangement,Recreational Vehicle,Renal and Blood Handling,Surgical Devices,Wireless Communications | |
Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm |