General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.35 g/cm³ Show Material materials with Density of 1.35 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.14 % Show Material materials with Water absorption of 0.14 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 4.2 GPa Show Material materials with Elastic modulus of 4.2 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 14 % Show Material materials with Elongation of 14 % | ISO 527 | 5 mm/min |
Elongation at yield | 23.0 °C | 3.3 % Show Material materials with Elongation at yield of 3.3 % | ISO 527 | 5 mm/min |
Flexural modulus | 23.0 °C | 4.1 GPa Show Material materials with Flexural modulus of 4.1 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 92 MPa Show Material materials with Flexural yield strength of 92 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 16 kJ/m² Show Material materials with Impact strength, Charpy notched of 16 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod notched of 5 kJ/m² | ISO 180/1A |
23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A | |
Impact strength, Izod unnotched | -30.0 °C | 80 kJ/m² Show Material materials with Impact strength, Izod unnotched of 80 kJ/m² | ISO 180/1U |
23.0 °C | 121 kJ/m² Show Material materials with Impact strength, Izod unnotched of 121 kJ/m² | ISO 180/1U | |
Tensile strength | 23.0 °C | 41 MPa Show Material materials with Tensile strength of 41 MPa | ISO 527 | 5 mm/min |
Yield strength | 23.0 °C | 56 MPa Show Material materials with Yield strength of 56 MPa | ISO 527 | 5 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 3.8E-5 1/K | ISO 11359-2 | -30°C to 80°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1E-4 1/K | ISO 11359-2 | -30°C to 80°C |
Heat deflection temperature, 1.80 MPa | 110 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 110 °C | ISO 75/Af | 1.8 MPa | |
Vicat softening temperature | 140 °C Show Material materials with Vicat softening temperature of 140 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 20 g/10min Show Material materials with Melt mass-flow rate of 20 g/10min | ASTM D 1238 | 265°C/5.0 kgf | |
Melt volume-flow rate | 16 cm³/10min Show Material materials with Melt volume-flow rate of 16 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Spoiler | |
Fillers | Mineral Powder | |
Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm |