XYLEX™ Resin X7300CL

Want to keep this datasheet? Save it now in your required format

Description

PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.2 g/cm³

Show Material materials with Density of 1.2 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.12 %

Show Material materials with Water absorption of 0.12 %

ISO 62 | 23°C, 50% RH

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.84 GPa

Show Material materials with Elastic modulus of 1.84 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

150 %

Show Material materials with Elongation of 150 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

5 %

Show Material materials with Elongation at yield of 5 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2 GPa

Show Material materials with Flexural modulus of 2 GPa

ISO 178 | 2 mm/min

Flexural strength

23.0 °C

71 MPa

Show Material materials with Flexural strength of 71 MPa

ISO 178

Flexural yield strength

23.0 °C

83 MPa

Show Material materials with Flexural yield strength of 83 MPa

ASTM D 790 | 1.3 mm/min, 50 mm span

Impact strength, Charpy notched

23.0 °C

11 kJ/m²

Show Material materials with Impact strength, Charpy notched of 11 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-30.0 °C

7 kJ/m²

Show Material materials with Impact strength, Izod notched of 7 kJ/m²

ISO 180/1A

-10.0 °C

5 kJ/m²

Show Material materials with Impact strength, Izod notched of 5 kJ/m²

ISO 180/1A

23.0 °C

10 kJ/m²

Show Material materials with Impact strength, Izod notched of 10 kJ/m²

ISO 180/1A

Impact strength, Izod notched, ASTM

-30.0 °C

56 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 56 J/m

ASTM D 256

23.0 °C

660 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 660 J/m

ASTM D 256

Unlock all property charts

Tensile strength

23.0 °C

52 MPa

Show Material materials with Tensile strength of 52 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

49 MPa

Show Material materials with Yield strength of 49 MPa

ASTM D 638 | Type I, 50 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.15E-4 1/K

Show Material materials with Coefficient of thermal expansion of 1.15E-4 1/K

ASTM E 831 | -40°C to 40°C

Coefficient of thermal expansion, transverse

23.0 °C

1.05E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.05E-4 1/K

ASTM E 831 | -40°C to 40°C

Heat deflection temperature, 1.80 MPa

88 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 88 °C

ASTM D 648 | 1.82 MPa, 3.2mm, unannealed

Vicat softening temperature

108 °C

Show Material materials with Vicat softening temperature of 108 °C

ASTM D 1525 | Rate B/50

Flammability

UL Recognized, 94V-2 Flame Class Rating | 3mm | UL 94

Optical

PropertyValueComment

Haze

2 %

Show Material materials with Haze of 2 %

ASTM D 1003 | 2.54 mm

Transmission

88 %

Show Material materials with Transmission of 88 %

ASTM D 1003 | 2.54 mm

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

44 g/10min

Show Material materials with Melt mass-flow rate of 44 g/10min

ASTM D 1238 | 300°C/1.2 kg

Melt volume-flow rate

42 cm³/10min

Show Material materials with Melt volume-flow rate of 42 cm³/10min

ISO 1133 | 300°C/1.2 kg

Shrinkage

23.0 °C

0.4 - 0.8 %

Show Material materials with Shrinkage of 0.4 - 0.8 %

SABIC method | 3.2 mm

Shrinkage, transverse

23.0 °C

0.5 - 0.7 %

Show Material materials with Shrinkage, transverse of 0.5 - 0.7 %

SABIC method

Technological properties

Property
Application areas

Data Management,Enclosure/Housing/Cover,Enclosures,Medical Device,Motorcycle,Non-LED Lighting,Personal Computing,Wireless Communications

Processing methods

Drying Temperature: 80-95°C, Drying Time: 3-5hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 250-270°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 245-265°C, Rear - Zone 1 Temperature: 240-250°C, Mold Temperature: 45-60°C, Back Pressure: 0.2-0.5MPa, Screw Speed: 20-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.02mm