General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Material materials with Elastic modulus of 2.3 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 130 % Show Material materials with Elongation of 130 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.18 GPa Show Material materials with Flexural modulus of 2.18 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 92 MPa Show Material materials with Flexural yield strength of 92 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 20 kJ/m² Show Material materials with Impact strength, Charpy notched of 20 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A |
23.0 °C | 9 kJ/m² Show Material materials with Impact strength, Izod notched of 9 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 200 J/m Show Material materials with Impact strength, Izod notched, ASTM of 200 J/m | ASTM D 256 |
23.0 °C | 990 J/m Show Material materials with Impact strength, Izod notched, ASTM of 990 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 65 MPa Show Material materials with Tensile strength of 65 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 61 MPa Show Material materials with Yield strength of 61 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6E-5 1/K Show Material materials with Coefficient of thermal expansion of 6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 104 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 104 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Vicat softening temperature | 125 °C Show Material materials with Vicat softening temperature of 125 °C | ASTM D 1525 | Rate B/50 |
Optical
Property | Value | Comment |
---|---|---|
Haze | 1.6 % Show Material materials with Haze of 1.6 % | ASTM D 1003 | 2.54 mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 8 g/10min Show Material materials with Melt mass-flow rate of 8 g/10min | ASTM D 1238 | 265°C/2.16kgf | |
Melt volume-flow rate | 5 cm³/10min Show Material materials with Melt volume-flow rate of 5 cm³/10min | ISO 1133 | 265°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.8 % Show Material materials with Shrinkage of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Enclosure/Housing/Cover,Fixture Bath/Shower,LED Lighting | |
Processing methods | Drying Temperature: 80-95°C, Drying Time: 3-5hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 250-270°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 245-265°C, Rear - Zone 1 Temperature: 240-250°C, Mold Temperature: 45-60°C, Back Pressure: 0.2-0.5MPa, Screw Speed: 20-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.02mm |