Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 1.48 GPa Show Material materials with Elastic modulus of 1.48 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 150 % Show Material materials with Elongation of 150 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 1.6 GPa Show Material materials with Flexural modulus of 1.6 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 58 MPa Show Material materials with Flexural strength of 58 MPa | ISO 178 |
Flexural yield strength | 23.0 °C | 65 MPa Show Material materials with Flexural yield strength of 65 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Charpy notched | 23.0 °C | 71 kJ/m² Show Material materials with Impact strength, Charpy notched of 71 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | -30.0 °C | 11 kJ/m² Show Material materials with Impact strength, Izod notched of 11 kJ/m² | ISO 180/1A |
-10.0 °C | 30 kJ/m² Show Material materials with Impact strength, Izod notched of 30 kJ/m² | ISO 180/1A | |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod notched of 45 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 200 J/m Show Material materials with Impact strength, Izod notched, ASTM of 200 J/m | ASTM D 256 |
-20.0 °C | 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 | |
23.0 °C | 800 J/m Show Material materials with Impact strength, Izod notched, ASTM of 800 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 46 MPa Show Material materials with Tensile strength of 46 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 43 MPa Show Material materials with Yield strength of 43 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-4 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 75 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 75 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Vicat softening temperature | 97 °C Show Material materials with Vicat softening temperature of 97 °C | ASTM D 1525 | Rate B/50 |
Optical
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 14 g/10min Show Material materials with Melt mass-flow rate of 14 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Melt volume-flow rate | 13 cm³/10min Show Material materials with Melt volume-flow rate of 13 cm³/10min | ISO 1133 | 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.8 % Show Material materials with Shrinkage of 0.5 - 0.8 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.4 - 0.6 % Show Material materials with Shrinkage, transverse of 0.4 - 0.6 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Audio,Data Management,Data Transfer,Displays,Document Handling,Electronic Components,Enclosures,Meter Water,Non-LED Lighting,Safety Glasses,Semiconductor,Wearables,Wireless Communications | |
Processing methods | Drying Temperature: 65-75°C, Drying Time: 3-5hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 245-265°C, Nozzle Temperature: 245-265°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-260°C, Rear - Zone 1 Temperature: 240-250°C, Mold Temperature: 45-60°C, Back Pressure: 0.2-0.5MPa, Screw Speed: 20-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.02mm |