General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.22 g/cm³ Show Material materials with Density of 1.22 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.1 % Show Material materials with Water absorption of 0.1 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 3.4 GPa Show Material materials with Elastic modulus of 3.4 GPa | ASTM D 638 | 5 mm/min | ||
Elongation | 23.0 °C | 100 % Show Material materials with Elongation of 100 % | ASTM D 638 | Type I, 5 mm/min | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 5 mm/min | ||
Flexural modulus | 23.0 °C | 3.1 GPa Show Material materials with Flexural modulus of 3.1 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 95 MPa Show Material materials with Flexural yield strength of 95 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Charpy notched | -30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | ||
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy notched of 45 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod notched of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Izod notched of 40 kJ/m² | ISO 180/1A | |||
Impact strength, Izod notched, ASTM | -30.0 °C | 120 J/m Show Material materials with Impact strength, Izod notched, ASTM of 120 J/m | ASTM D 256 | ||
23.0 °C | 500 J/m Show Material materials with Impact strength, Izod notched, ASTM of 500 J/m | ASTM D 256 | |||
Tensile strength | 23.0 °C | 55 MPa Show Material materials with Tensile strength of 55 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Yield strength | 23.0 °C | 60 MPa Show Material materials with Yield strength of 60 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Impact strength, Charpy unnotched | No break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No break @ 23,-30°C | ISO 180/1U |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6E-5 1/K Show Material materials with Coefficient of thermal expansion of 6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 118 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 |
Vicat softening temperature | 138 °C Show Material materials with Vicat softening temperature of 138 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 11 g/10min Show Material materials with Melt mass-flow rate of 11 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Melt volume-flow rate | 9 cm³/10min Show Material materials with Melt volume-flow rate of 9 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.7 - 0.8 % Show Material materials with Shrinkage of 0.7 - 0.8 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket | |
Processing methods | Drying Temperature: 120-110°C, Drying Time: 2-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 270-300°C, Nozzle Temperature: 260-290°C, Front - Zone 3 Temperature: 270-300°C, Middle - Zone 2 Temperature: 265-290°C, Rear - Zone 1 Temperature: 260-270°C, Mold Temperature: 60-100°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm |