Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.14 g/cm³ Show Material materials with Density of 1.14 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.13 % Show Material materials with Water absorption of 0.13 % | ISO 62 | 23°C, 50% RH |
Mechanical
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.2 GPa Show Material materials with Elastic modulus of 2.2 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 100 % Show Material materials with Elongation of 100 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527 | 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.2 GPa Show Material materials with Flexural modulus of 2.2 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 82 MPa Show Material materials with Flexural yield strength of 82 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Charpy notched | -30.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy notched of 45 kJ/m² | ISO 179/1eA | ||
23.0 °C | 60 kJ/m² Show Material materials with Impact strength, Charpy notched of 60 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -30.0 °C | 40 kJ/m² Show Material materials with Impact strength, Izod notched of 40 kJ/m² | ISO 180/1A | ||
23.0 °C | 55 kJ/m² Show Material materials with Impact strength, Izod notched of 55 kJ/m² | ISO 180/1A | |||
Tensile strength | 23.0 °C | 56 MPa Show Material materials with Tensile strength of 56 MPa | ISO 527 | 50 mm/min | ||
Yield strength | 23.0 °C | 54 MPa Show Material materials with Yield strength of 54 MPa | ISO 527 | 50 mm/min | ||
Impact strength, Charpy unnotched | No break @ 23°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No break @ 23°C | ISO 180/1U | ||||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 126 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 126 °C | ISO 75/Bf | 0.45 MPa | |
Vicat softening temperature | 129 °C Show Material materials with Vicat softening temperature of 129 °C | ASTM D 1525 | Rate B/50 |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt volume-flow rate | 25 cm³/10min Show Material materials with Melt volume-flow rate of 25 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage, transverse of 0.5 - 0.7 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Interior | |
| Processing methods | Drying Temperature: 95-105°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 240-280°C, Front - Zone 3 Temperature: 250-290°C, Middle - Zone 2 Temperature: 250-290°C, Rear - Zone 1 Temperature: 230-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C | |