Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.14 g/cm³ Show Material materials with Density of 1.14 g/cm³ | ASTM D 792 |
Water absorption | 23.0 °C | 0.15 % Show Material materials with Water absorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Material materials with Elastic modulus of 2.3 GPa | ASTM D 638 | 5 mm/min |
Elongation | 23.0 °C | 120 % Show Material materials with Elongation of 120 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural modulus | 23.0 °C | 2.2 GPa Show Material materials with Flexural modulus of 2.2 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 82 MPa Show Material materials with Flexural yield strength of 82 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | -30.0 °C | 30 kJ/m² Show Material materials with Impact strength, Charpy notched of 30 kJ/m² | ISO 179/1eA |
23.0 °C | 65 kJ/m² Show Material materials with Impact strength, Charpy notched of 65 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -30.0 °C | 30 kJ/m² Show Material materials with Impact strength, Izod notched of 30 kJ/m² | ISO 180/1A |
23.0 °C | 65 kJ/m² Show Material materials with Impact strength, Izod notched of 65 kJ/m² | ISO 180/1A | |
Impact strength, Izod notched, ASTM | -30.0 °C | 430 J/m Show Material materials with Impact strength, Izod notched, ASTM of 430 J/m | ASTM D 256 |
23.0 °C | 590 J/m Show Material materials with Impact strength, Izod notched, ASTM of 590 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 53 MPa Show Material materials with Tensile strength of 53 MPa | ASTM D 638 | Type I, 50 mm/min |
Yield strength | 23.0 °C | 54 MPa Show Material materials with Yield strength of 54 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 126 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 126 °C | ISO 75/Bf | 0.45 MPa | |
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 |
Vicat softening temperature | 126 °C Show Material materials with Vicat softening temperature of 126 °C | ASTM D 1525 | Rate B/50 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 26 g/10min Show Material materials with Melt mass-flow rate of 26 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Melt viscosity | 260.0 °C | 170 Pa·s Show Material materials with Melt viscosity of 170 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Melt volume-flow rate | 22 cm³/10min Show Material materials with Melt volume-flow rate of 22 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.5 - 0.7 % Show Material materials with Shrinkage, transverse of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Circuit Protection,Cluster,Console,Door Handle,Doors Hardware/Trim,Electronic Components,Enclosures,EV Infrastructure,Exterior Trim,Exterior,Forward Lighting,Front Grille,Glove Box,HVAC Underhood,Infotainment/Telematic,Interior,Meter Gas,Rear/Signal Lighting,Seat,Spoiler,Trim | |
Processing methods | Drying Temperature: 95-105°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 240-280°C, Front - Zone 3 Temperature: 250-290°C, Middle - Zone 2 Temperature: 250-290°C, Rear - Zone 1 Temperature: 230-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C |