XENOY™ Resin XL1339

Want to keep this datasheet? Save it now in your required format

Description

Data generated in BOZ labs. High heat grade for nonchemical resistance required applications.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.22 g/cm³

Show Material materials with Density of 1.22 g/cm³

ASTM D 792

Water absorption

23.0 °C

0.2 %

Show Material materials with Water absorption of 0.2 %

ASTM D 570 | 50% RH, equilib

Water absorption, equilibrium

23.0 °C

0.7 %

Show Material materials with Water absorption, equilibrium of 0.7 %

ASTM D 570

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

2.09 GPa

Show Material materials with Elastic modulus of 2.09 GPa

ASTM D 638 | 50 mm/min

Elongation

23.0 °C

110 %

Show Material materials with Elongation of 110 %

ASTM D 638 | Type I, 50 mm/min

Elongation at yield

23.0 °C

5 %

Show Material materials with Elongation at yield of 5 %

ASTM D 638 | Type I, 50 mm/min

Flexural modulus

23.0 °C

2.2 GPa

Show Material materials with Flexural modulus of 2.2 GPa

ISO 178 | 2 mm/min

Flexural yield strength

23.0 °C

80 MPa

Show Material materials with Flexural yield strength of 80 MPa

ISO 178 | 2 mm/min

Impact strength, Charpy notched

-30.0 °C

35 kJ/m²

Show Material materials with Impact strength, Charpy notched of 35 kJ/m²

ISO 179/1eA

23.0 °C

45 kJ/m²

Show Material materials with Impact strength, Charpy notched of 45 kJ/m²

ISO 179/1eA

Impact strength, Izod notched

-40.0 °C

15 kJ/m²

Show Material materials with Impact strength, Izod notched of 15 kJ/m²

ISO 180/1A

-30.0 °C

25 kJ/m²

Show Material materials with Impact strength, Izod notched of 25 kJ/m²

ISO 180/1A

-20.0 °C

35 kJ/m²

Show Material materials with Impact strength, Izod notched of 35 kJ/m²

ISO 180/1A

-10.0 °C

38 kJ/m²

Show Material materials with Impact strength, Izod notched of 38 kJ/m²

ISO 180/1A

23.0 °C

40 kJ/m²

Show Material materials with Impact strength, Izod notched of 40 kJ/m²

ISO 180/1A

Unlock all property charts

Impact strength, Izod notched, ASTM

-40.0 °C

224 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 224 J/m

ASTM D 256

-30.0 °C

245 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 245 J/m

ASTM D 256

-20.0 °C

598 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 598 J/m

ASTM D 256

23.0 °C

699 J/m

Show Material materials with Impact strength, Izod notched, ASTM of 699 J/m

ASTM D 256

Unlock all property charts

Poisson's ratio

23.0 °C

0.4 [-]

Show Material materials with Poisson's ratio of 0.4 [-]

ASTM E 132

Tensile strength

23.0 °C

49 MPa

Show Material materials with Tensile strength of 49 MPa

ASTM D 638 | Type I, 50 mm/min

Yield strength

23.0 °C

49 MPa

Show Material materials with Yield strength of 49 MPa

ASTM D 638 | Type I, 50 mm/min

Impact strength, Charpy unnotched

No break @ 23,-30°C | ISO 179/1eU

Impact strength, Izod unnotched

No break @ 23,-30°C | ISO 180/1U

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

7.56E-5 1/K

Show Material materials with Coefficient of thermal expansion of 7.56E-5 1/K

ASTM D 696 | -30°C to 30°C

Coefficient of thermal expansion, transverse

23.0 °C

7.92E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 7.92E-5 1/K

ASTM D 696 | -30°C to 30°C

Heat deflection temperature, 1.80 MPa

105 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 105 °C

ISO 75/Ae | 1.8 MPa

Thermal conductivity

23.0 °C

0.18 W/(m·K)

Show Material materials with Thermal conductivity of 0.18 W/(m·K)

ASTM C177

Vicat softening temperature

135 °C

Show Material materials with Vicat softening temperature of 135 °C

ISO 306 | Rate B/120

Electrical

PropertyTemperatureValueComment

Dielectric constant

23.0 °C

3.1 [-]

Show Material materials with Dielectric constant of 3.1 [-]

ASTM D 150 | at 1 MHz

Dielectric strength

23.0 °C

16.9 kV/mm

Show Material materials with Dielectric strength of 16.9 kV/mm

ASTM D 149 | in oil, 3.2 mm

Dissipation factor

23.0 °C

0.02 [-]

Show Material materials with Dissipation factor of 0.02 [-]

ASTM D 150 | at 1 MHz

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

4 cm³/10min

Show Material materials with Melt volume-flow rate of 4 cm³/10min

ISO 1133 | 265°C/1.2 kg

Shrinkage

23.0 °C

0.5 - 0.8 %

Show Material materials with Shrinkage of 0.5 - 0.8 %

SABIC method

Shrinkage, transverse

23.0 °C

0.5 - 0.8 %

Show Material materials with Shrinkage, transverse of 0.5 - 0.8 %

SABIC method

Technological properties

Property
Application areas

Door Handle,Wiring Devices

Processing methods

Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-275°C, Nozzle Temperature: 255-270°C, Front - Zone 3 Temperature: 255-275°C, Middle - Zone 2 Temperature: 250-270°C, Rear - Zone 1 Temperature: 245-265°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm