Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.15 g/cm³ Show Material materials with Density of 1.15 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.25 % Show Material materials with Water absorption of 0.25 % | ISO 62 | 23°C, 50% RH |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Material materials with Elastic modulus of 2.4 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 15 % Show Material materials with Elongation of 15 % | ISO 527 | 50 mm/min | ||
Elongation at yield | 23.0 °C | 4.1 % Show Material materials with Elongation at yield of 4.1 % | ISO 527 | 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.4 GPa Show Material materials with Flexural modulus of 2.4 GPa | ISO 178 | 2 mm/min | ||
Flexural yield strength | 23.0 °C | 80 MPa Show Material materials with Flexural yield strength of 80 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 98 MPa Show Material materials with Hardness, Ball Indentation of 98 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 115 [-] Show Material materials with Hardness, Rockwell R of 115 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | -30.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA | ||
23.0 °C | 14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod notched | -40.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A | ||
-30.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod notched of 6 kJ/m² | ISO 180/1A | |||
-10.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A | |||
23.0 °C | 15 kJ/m² Show Material materials with Impact strength, Izod notched of 15 kJ/m² | ISO 180/1A | |||
Tensile strength | 23.0 °C | 45 MPa Show Material materials with Tensile strength of 45 MPa | ISO 527 | 50 mm/min | ||
Yield strength | 23.0 °C | 58 MPa Show Material materials with Yield strength of 58 MPa | ISO 527 | 50 mm/min | ||
Impact strength, Charpy unnotched | No break @ 23,-30°C | ISO 179/1eU | ||||
Impact strength, Izod unnotched | No break @ 23,-30°C | ISO 180/1U |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Material materials with Coefficient of thermal expansion of 7E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 9E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature, 1.80 MPa | 86 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 86 °C | ISO 75/Ae | 1.8 MPa | |||
Relative temperature index, electrical | 50 °C Show Material materials with Relative temperature index, electrical of 50 °C | UL 746B | |||
Relative temperature index, mechanical impact | 50 °C Show Material materials with Relative temperature index, mechanical impact of 50 °C | UL 746B | |||
Relative temperature index, mechanical strength | 50 °C Show Material materials with Relative temperature index, mechanical strength of 50 °C | UL 746B | |||
Thermal conductivity | 23.0 °C | 0.24 W/(m·K) Show Material materials with Thermal conductivity of 0.24 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 107 °C Show Material materials with Vicat softening temperature of 107 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Recognized, 94HB Flame Class Rating 2nd value | 3mm | UL 94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 225 V Show Material materials with Comparative tracking index of 225 V | IEC 60112 |
Dielectric constant | 23.0 °C | 4.3 [-] Show Material materials with Dielectric constant of 4.3 [-] | IEC 60250 | at 50/60 Hz |
Dielectric strength | 23.0 °C | 27 kV/mm Show Material materials with Dielectric strength of 27 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Dissipation factor | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor of 0.02 [-] | IEC 60250 | at 1 MHz |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 18 cm³/10min Show Material materials with Melt volume-flow rate of 18 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.4 - 0.6 % Show Material materials with Shrinkage of 0.4 - 0.6 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Applique,Cluster,Data Transfer,Electronic Components,Enclosure/Housing/Cover,Enclosures,Exterior Mirror,Exterior Trim,Exterior,Front Grille,Heavy Vehicles,Motorcycle,Overhead,Plumbing,Rear/Signal Lighting,Recreational Vehicle,Spoiler | |
Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.05%, Melt Temperature: 250-270°C, Nozzle Temperature: 230-260°C, Front - Zone 3 Temperature: 240-270°C, Middle - Zone 2 Temperature: 230-260°C, Rear - Zone 1 Temperature: 220-250°C, Hopper Temperature: 60-80°C, Mold Temperature: 50-70°C |