Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Material materials with Density of 1.19 g/cm³ | ISO 1183 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 2.32 GPa Show Material materials with Elastic modulus of 2.32 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 46.7 % Show Material materials with Elongation of 46.7 % | ISO 527 | 50 mm/min |
Elongation at yield | 23.0 °C | 5.2 % Show Material materials with Elongation at yield of 5.2 % | ISO 527 | 50 mm/min |
Flexural modulus | 23.0 °C | 2.27 GPa Show Material materials with Flexural modulus of 2.27 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 93 MPa Show Material materials with Flexural yield strength of 93 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | -40.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA |
-30.0 °C | 14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA | |
23.0 °C | 25 kJ/m² Show Material materials with Impact strength, Charpy notched of 25 kJ/m² | ISO 179/1eA | |
Impact strength, Izod notched | -40.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A |
-30.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A | |
23.0 °C | 14 kJ/m² Show Material materials with Impact strength, Izod notched of 14 kJ/m² | ISO 180/1A | |
Tensile strength | 23.0 °C | 45 MPa Show Material materials with Tensile strength of 45 MPa | ISO 527 | 50 mm/min |
Yield strength | 23.0 °C | 60 MPa Show Material materials with Yield strength of 60 MPa | ISO 527 | 50 mm/min |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.7E-5 1/K Show Material materials with Coefficient of thermal expansion of 6.7E-5 1/K | ISO 11359-2 | -30°C to 80°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 7.6E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7.6E-5 1/K | ISO 11359-2 | -30°C to 80°C |
Heat deflection temperature, 0.45 MPa | 125 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 125 °C | ISO 75/Bf | 0.45 MPa | |
Vicat softening temperature | 126 °C Show Material materials with Vicat softening temperature of 126 °C | ISO 306 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt volume-flow rate | 28 cm³/10min Show Material materials with Melt volume-flow rate of 28 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.6 - 0.9 % Show Material materials with Shrinkage of 0.6 - 0.9 % | SABIC method | 3.2 mm |
Shrinkage, transverse | 23.0 °C | 0.6 - 0.9 % Show Material materials with Shrinkage, transverse of 0.6 - 0.9 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Exterior Mirror,Overhead | |
| Processing methods | Drying Temperature: 95-105°C, Drying Time: 3-4hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 265-285°C, Nozzle Temperature: 260-275°C, Front - Zone 3 Temperature: 240-270°C, Middle - Zone 2 Temperature: 250-275°C, Rear - Zone 1 Temperature: 260-280°C, Mold Temperature: 50-80°C, Back Pressure: 0.3-1MPa, Screw Speed: 30-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.038-0.076mm | |