General
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.46 GPa Show Material materials with Elastic modulus of 2.46 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 20 % Show Material materials with Elongation of 20 % | ISO 527 | 50 mm/min |
Elongation at yield | 23.0 °C | 3.7 % Show Material materials with Elongation at yield of 3.7 % | ISO 527 | 50 mm/min |
Flexural modulus | 23.0 °C | 2.5 GPa Show Material materials with Flexural modulus of 2.5 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 82 MPa Show Material materials with Flexural yield strength of 82 MPa | ISO 178 | 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 92 MPa Show Material materials with Hardness, Ball Indentation of 92 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 111 [-] Show Material materials with Hardness, Rockwell R of 111 [-] | ISO 2039-2 |
Impact strength, Izod notched | -30.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod notched of 8 kJ/m² | ISO 180/1A |
23.0 °C | 20 kJ/m² Show Material materials with Impact strength, Izod notched of 20 kJ/m² | ISO 180/1A | |
Tensile strength | 23.0 °C | 43 MPa Show Material materials with Tensile strength of 43 MPa | ISO 527 | 50 mm/min |
Yield strength | 23.0 °C | 55 MPa Show Material materials with Yield strength of 55 MPa | ISO 527 | 50 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 9.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 9.5E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature, 1.80 MPa | 86 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 86 °C | ISO 75/Ae | 1.8 MPa | |||
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 107 °C Show Material materials with Vicat softening temperature of 107 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Compliant, 94HB Flame Class Rating | 3.2mm | UL 94 by SABIC-IP |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 20 cm³/10min Show Material materials with Melt volume-flow rate of 20 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Shrinkage | 23.0 °C | 0.4 - 0.6 % Show Material materials with Shrinkage of 0.4 - 0.6 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Front Grille,Spoiler | |
Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.05%, Melt Temperature: 250-270°C, Nozzle Temperature: 230-260°C, Front - Zone 3 Temperature: 240-270°C, Middle - Zone 2 Temperature: 230-260°C, Rear - Zone 1 Temperature: 220-250°C, Hopper Temperature: 60-80°C, Mold Temperature: 50-70°C |