General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.18 g/cm³ Show Material materials with Density of 1.18 g/cm³ | ISO 1183 |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 2.68 GPa Show Material materials with Elastic modulus of 2.68 GPa | ASTM D 638 | 50 mm/min |
Elongation | 23.0 °C | 58 % Show Material materials with Elongation of 58 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ASTM D 638 | Type I, 5 mm/min |
Flexural modulus | 23.0 °C | 2.72 GPa Show Material materials with Flexural modulus of 2.72 GPa | ISO 178 | 2 mm/min |
Flexural yield strength | 23.0 °C | 97 MPa Show Material materials with Flexural yield strength of 97 MPa | ISO 178 | 2 mm/min |
Impact strength, Charpy notched | 23.0 °C | 13 kJ/m² Show Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA |
Impact strength, Izod notched | 23.0 °C | 12 - 13 kJ/m² Show Material materials with Impact strength, Izod notched of 12 - 13 kJ/m² | ISO 180/1A |
Impact strength, Izod notched, ASTM | -30.0 °C | 90 J/m Show Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 |
23.0 °C | 330 J/m Show Material materials with Impact strength, Izod notched, ASTM of 330 J/m | ASTM D 256 | |
Tensile strength | 23.0 °C | 49 MPa Show Material materials with Tensile strength of 49 MPa | ASTM D 638 | Type I, 5 mm/min |
Yield strength | 23.0 °C | 60 MPa Show Material materials with Yield strength of 60 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 6.3E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.3E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6.3E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 90 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 90 °C | ISO 75/Bf | 0.45 MPa | |||
Vicat softening temperature | 98 °C Show Material materials with Vicat softening temperature of 98 °C | ISO 306 | Rate B/120 | |||
Flammability | UL Compliant, 94V-0 Flame Class Rating | 1mm | UL 94 by SABIC-IP | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 260.0 °C | 105 Pa·s Show Material materials with Melt viscosity of 105 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Melt volume-flow rate | 30 cm³/10min Show Material materials with Melt volume-flow rate of 30 cm³/10min | ISO 1133 | 260°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Building Accessory,Cladding/Roof,Data Transfer,Dishwasher,Enclosure/Housing/Cover,Enclosures,Heavy Vehicles,Medical Device,Wireless Communications | |
| Processing methods | Drying Temperature: 80-90°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 230-270°C, Nozzle Temperature: 220-260°C, Front - Zone 3 Temperature: 230-270°C, Middle - Zone 2 Temperature: 220-260°C, Rear - Zone 1 Temperature: 200-230°C, Hopper Temperature: 60-80°C, Mold Temperature: 50-70°C | |