General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.3 g/cm³ Show Material materials with Density of 1.3 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.6 GPa Show Material materials with Elastic modulus of 2.6 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 110 % Show Material materials with Elongation of 110 % | ISO 527-1/-2 | 50mm/min |
Elongation at yield | 23.0 °C | 8 % Show Material materials with Elongation at yield of 8 % | ISO 527-1/-2 |
Impact strength, Charpy notched | -6.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 4.5 kJ/m² | ISO 179/1eA |
23.0 °C | 5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA | |
Impact strength, Izod unnotched | 23.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.38 [-] Show Material materials with Poisson's ratio of 0.38 [-] | |
Yield strength | 23.0 °C | 59 MPa Show Material materials with Yield strength of 59 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.4E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.4E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 180 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 180 °C | ISO 75-1/-2 | annealed | |||
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75-1/-2 | annealed | |||
Melting point | 225 °C Show Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 2050 J/(kg·K) Show Material materials with Specific heat capacity of 2050 J/(kg·K) | of melt | ||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, UL recognition: yes -, Oxygen index: 22 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 1MHz | 23.0 °C | 3.2 [-] Show Material materials with Dielectric constant, 1MHz of 3.2 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 26 kV/mm Show Material materials with Dielectric strength of 26 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 16 g/10min Show Material materials with Melt mass-flow rate of 16 g/10min | ISO 1133 | 250°C/2.16kg | |
Melt volume-flow rate | 14 cm³/10min Show Material materials with Melt volume-flow rate of 14 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.7 % Show Material materials with Shrinkage of 1.7 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.7 % Show Material materials with Shrinkage, transverse of 1.7 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |