General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.21 g/cm³ Show Material materials with Density of 1.21 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 1.6 GPa Show Material materials with Elastic modulus of 1.6 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 30 % Show Material materials with Elongation of 30 % | ISO 527-1/-2 | 50mm/min | ||
Elongation at yield | 23.0 °C | 9 % Show Material materials with Elongation at yield of 9 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 1.6 GPa Show Material materials with Flexural modulus of 1.6 GPa | ISO 178 | ||
Flexural strength | 23.0 °C | 50 MPa Show Material materials with Flexural strength of 50 MPa | ISO 178 | ||
Impact strength, Charpy notched | -40.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA | ||
-6.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |||
23.0 °C | 120 kJ/m² Show Material materials with Impact strength, Charpy notched of 120 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod unnotched | -40.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod unnotched of 10 kJ/m² | ISO 180/1A | ||
23.0 °C | 90 kJ/m² Show Material materials with Impact strength, Izod unnotched of 90 kJ/m² | ISO 180/1A | |||
Poisson's ratio | 23.0 °C | 0.42 [-] Show Material materials with Poisson's ratio of 0.42 [-] | |||
Tensile strength | 23.0 °C | 30 MPa Show Material materials with Tensile strength of 30 MPa | ISO 527-1/-2 | 50mm/min | ||
Yield strength | 23.0 °C | 34 MPa Show Material materials with Yield strength of 34 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 130 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 130 °C | ISO 75-1/-2 | annealed | |||
Heat deflection temperature, 1.80 MPa | 50 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 50 °C | ISO 75-1/-2 | |||
Melting point | 220 °C Show Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 18°F/min | |||
Specific heat capacity | 23.0 °C | 2210 J/(kg·K) Show Material materials with Specific heat capacity of 2210 J/(kg·K) | of melt | ||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 40 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 31 kV/mm Show Material materials with Dielectric strength of 31 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 7E-3 [-] Show Material materials with Dissipation factor, 100Hz of 7E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Back pressure: As low as possible |