Crastin® LW9320LM BK591

Alternative and trade names
PBT+SAN-GF20
Want to keep this datasheet? Save it now in your required format

Description

Common features of Crastin® thermoplastic polyester resin include mechanical and physical properties such as stiffness and toughness, heat resistance, friction and wear resistance, excellent surface finishes and good colourability. Crastin® thermoplastic polyester resin has excellent electrical insulation characteristics and high arc-resistant grades are available. Many flame retardant grades have UL recognition (class V-0). Crastin® thermoplastic polyester resin typically has high chemical and heat ageing resistance. The good melt stability of Crastin® thermoplastic polyester resin normally enables the recycling of properly handled production waste.If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-24 kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed. Crastin® thermoplastic polyester resin typically is used in demanding applications in the electronics, electrical, automotive, mechanical engineering, chemical, domestic appliances and sporting goods industry.Crastin® LW9320LM is a 20% glass fiber reinforced polybutylene terephthalate blend for injection molding. It has excellent surface aspect, dimensional stability and low warpage and was developed for laser marking applications..

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.35 g/cm³

Show Material materials with Density of 1.35 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

7.5 GPa

Show Material materials with Elastic modulus of 7.5 GPa

ISO 527-1/-2

Elongation

23.0 °C

2.3 %

Show Material materials with Elongation of 2.3 %

ISO 527-1/-2

Flexural modulus

23.0 °C

7 GPa

Show Material materials with Flexural modulus of 7 GPa

ISO 178

Impact strength, Charpy notched

23.0 °C

7 kJ/m²

Show Material materials with Impact strength, Charpy notched of 7 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

-6.0 °C

40 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m²

ISO 179/1eU

23.0 °C

45 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m²

ISO 179/1eU

Impact strength, Izod notched

-40.0 °C

45 kJ/m²

Show Material materials with Impact strength, Izod notched of 45 kJ/m²

ISO 180/1U

23.0 °C

45 kJ/m²

Show Material materials with Impact strength, Izod notched of 45 kJ/m²

ISO 180/1U

Unlock all property charts

Poisson's ratio

23.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

23.0 °C

120 MPa

Show Material materials with Tensile strength of 120 MPa

ISO 527-1/-2

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

165 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 165 °C

ISO 75-1/-2

Melting point

220 °C

Show Material materials with Melting point of 220 °C

ISO 11357-1/-3 | 18°F/min

Flammability

Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.6 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: 59 mm/min

Technological properties

Property
Fillers

20% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C