General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.37 g/cm³ Show Material materials with Density of 1.37 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.08 % Show Material materials with Water absorption of 0.08 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 5.2 GPa Show Material materials with Elastic modulus of 5.2 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.4 % Show Material materials with Elongation of 3.4 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 4.7 GPa Show Material materials with Flexural modulus of 4.7 GPa | ISO 178 |
Hardness, Rockwell R | 23.0 °C | 117 [-] Show Material materials with Hardness, Rockwell R of 117 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -6.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 50 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 50 kJ/m² | ISO 179/1eU |
Impact strength, Izod notched | 23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Izod notched of 40 kJ/m² | ISO 180/1U |
Impact strength, Izod unnotched | -40.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod unnotched of 6 kJ/m² | ISO 180/1A |
23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod unnotched of 10 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.35 [-] Show Material materials with Poisson's ratio of 0.35 [-] | |
Tensile strength | 23.0 °C | 92 MPa Show Material materials with Tensile strength of 92 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 220 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 220 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 200 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75-1/-2 | |
Melting point | 225 °C Show Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 18°F/min | |
Flammability | Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, Oxygen index: 20 %, Glow Wire Flammability Index, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 32 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 300 V Show Material materials with Comparative tracking index of 300 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 3.8 [-] Show Material materials with Dielectric constant, 100Hz of 3.8 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.7 [-] Show Material materials with Dielectric constant, 1MHz of 3.7 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 36 kV/mm Show Material materials with Dielectric strength of 36 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 2.3E-3 [-] Show Material materials with Dissipation factor, 100Hz of 2.3E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 23 g/10min Show Material materials with Melt mass-flow rate of 23 g/10min | ISO 1133 | 250°C/2.16kg | |
Shrinkage | 23.0 °C | 0.5 % Show Material materials with Shrinkage of 0.5 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.1 % Show Material materials with Shrinkage, transverse of 1.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 15% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |