General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.55 g/cm³ Show Material materials with Density of 1.55 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.2 GPa Show Material materials with Elastic modulus of 10.2 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 1.7 % Show Material materials with Elongation of 1.7 % | ISO 527-1/-2 |
Flexural strength | 23.0 °C | 160 MPa Show Material materials with Flexural strength of 160 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 35 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 35 kJ/m² | ISO 179/1eU |
Impact strength, Izod unnotched | 23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod unnotched of 6 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 115 MPa Show Material materials with Tensile strength of 115 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Melting point | 225 °C Show Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 18°F/min | |
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 240mil | |
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 240mil | |
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 240mil | |
Flammability | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.75 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 2 mm, UL recognition: yes -, Oxygen index: 27 %, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 120mil: 960 °C, FMVSS Class: DNI - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 325 V Show Material materials with Comparative tracking index of 325 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.7 [-] Show Material materials with Dielectric constant, 100Hz of 4.7 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.4 [-] Show Material materials with Dielectric constant, 1MHz of 4.4 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 29 kV/mm Show Material materials with Dielectric strength of 29 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 5.4E-3 [-] Show Material materials with Dissipation factor, 100Hz of 5.4E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Melt mass-flow rate | 14 g/10min Show Material materials with Melt mass-flow rate of 14 g/10min | ISO 1133 | 250°C/5kg |
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |