General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.34 g/cm³ Show Material materials with Density of 1.34 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 7.5 GPa Show Material materials with Elastic modulus of 7.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.5 % Show Material materials with Elongation of 2.5 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 6.5 GPa Show Material materials with Flexural modulus of 6.5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 170 MPa Show Material materials with Flexural strength of 170 MPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 8.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 8.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU |
23.0 °C | 50 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 50 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -40.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod notched of 45 kJ/m² | ISO 180/1U |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod notched of 45 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | -40.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod unnotched of 7 kJ/m² | ISO 180/1A |
-30.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod unnotched of 7 kJ/m² | ISO 180/1A | |
23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod unnotched of 7 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 120 MPa Show Material materials with Tensile strength of 120 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3E-5 1/K Show Material materials with Coefficient of thermal expansion of 3E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1E-4 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | 110 °C Show Material materials with Glass transition temperature of 110 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 175 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 175 °C | ISO 75-1/-2 | |||
Melting point | 220 °C Show Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 1900 J/(kg·K) Show Material materials with Specific heat capacity of 1900 J/(kg·K) | of melt | ||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 31 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 500 V Show Material materials with Comparative tracking index of 500 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 15 cm³/10min Show Material materials with Melt volume-flow rate of 15 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 0.4 % Show Material materials with Shrinkage of 0.4 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 0.7 % Show Material materials with Shrinkage, transverse of 0.7 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 20% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |