General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.34 g/cm³ Show Material materials with Density of 1.34 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 7.5 GPa Show Material materials with Elastic modulus of 7.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.3 % Show Material materials with Elongation of 2.3 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 7 GPa Show Material materials with Flexural modulus of 7 GPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | -6.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU | |
Impact strength, Izod unnotched | 23.0 °C | 6.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 6.5 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 120 MPa Show Material materials with Tensile strength of 120 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 165 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 165 °C | ISO 75-1/-2 | |
Melting point | 220 °C Show Material materials with Melting point of 220 °C | ISO 11357-1/-3 | 18°F/min | |
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 32 mm/min |
Technological properties
Property | ||
---|---|---|
Fillers | 20% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |