Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 8.5 GPa Show Material materials with Elastic modulus of 8.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.2 % Show Material materials with Elongation of 3.2 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 7.5 GPa Show Material materials with Flexural modulus of 7.5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 200 MPa Show Material materials with Flexural strength of 200 MPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 11.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 11.5 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 70 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 70 kJ/m² | ISO 179/1eU |
Impact strength, Izod notched | 23.0 °C | 65 kJ/m² Show Material materials with Impact strength, Izod notched of 65 kJ/m² | ISO 180/1U |
Impact strength, Izod unnotched | -40.0 °C | 11 kJ/m² Show Material materials with Impact strength, Izod unnotched of 11 kJ/m² | ISO 180/1A |
23.0 °C | 14 kJ/m² Show Material materials with Impact strength, Izod unnotched of 14 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Shear strength | 23.0 °C | 55 MPa Show Material materials with Shear strength of 55 MPa | ASTM D 732 |
Tensile strength | 23.0 °C | 125 MPa Show Material materials with Tensile strength of 125 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.5E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.5E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.5E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Glass transition temperature | 65 °C Show Material materials with Glass transition temperature of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 221 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 221 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 207 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 207 °C | ISO 75-1/-2 | |||
Melting point | 225 °C Show Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | 30mil | |||
Specific heat capacity | 23.0 °C | 1730 J/(kg·K) Show Material materials with Specific heat capacity of 1730 J/(kg·K) | of melt | ||
Vicat softening temperature | 215 °C Show Material materials with Vicat softening temperature of 215 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 19 %, Glow Wire Flammability Index, 120mil: 750 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 30 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 450 V Show Material materials with Comparative tracking index of 450 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.4 [-] Show Material materials with Dielectric constant, 100Hz of 4.4 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.1 [-] Show Material materials with Dielectric constant, 1MHz of 4.1 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 19 kV/mm Show Material materials with Dielectric strength of 19 kV/mm | IEC 60243-1 | Short Time, 2mm |
Dissipation factor, 100Hz | 23.0 °C | 2.5E-3 [-] Show Material materials with Dissipation factor, 100Hz of 2.5E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Material materials with Surface resistivity of 1.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 8 cm³/10min Show Material materials with Melt volume-flow rate of 8 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 0.3 % Show Material materials with Shrinkage of 0.3 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1 % Show Material materials with Shrinkage, transverse of 1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |