General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.45 g/cm³ Show Material materials with Density of 1.45 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.35 % Show Material materials with Water absorption of 0.35 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.5 GPa Show Material materials with Elastic modulus of 3.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 10 % Show Material materials with Elongation of 10 % | ISO 527-1/-2 |
Flexural strength | 23.0 °C | 90 MPa Show Material materials with Flexural strength of 90 MPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 3.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 3.5 kJ/m² | ISO 179/1eA |
23.0 °C | 3.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 3.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 50 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 50 kJ/m² | ISO 179/1eU |
23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 34 kJ/m² Show Material materials with Impact strength, Izod notched of 34 kJ/m² | ISO 180/1U |
23.0 °C | 37 kJ/m² Show Material materials with Impact strength, Izod notched of 37 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | -30.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4 kJ/m² | ISO 180/1A |
23.0 °C | 3.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 3.5 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |
Tensile strength | 23.0 °C | 47 MPa Show Material materials with Tensile strength of 47 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 165 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 165 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 65 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 65 °C | ISO 75-1/-2 | |||
Melting point | 225 °C Show Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 115 °C Show Material materials with Relative temperature index, mechanical impact of 115 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 120 °C Show Material materials with Relative temperature index, mechanical strength of 120 °C | UL 746B | 240mil | |||
Specific heat capacity | 23.0 °C | 1850 J/(kg·K) Show Material materials with Specific heat capacity of 1850 J/(kg·K) | of melt | ||
Vicat softening temperature | 195 °C Show Material materials with Vicat softening temperature of 195 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 22 %, Glow Wire Flammability Index, 120mil: 750 °C, FMVSS Class: SE -, Burning rate, Thickness 1 mm: 24 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 250 V Show Material materials with Comparative tracking index of 250 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4 [-] Show Material materials with Dielectric constant, 100Hz of 4 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.7 [-] Show Material materials with Dielectric constant, 1MHz of 3.7 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | Short Time, 2mm |
Dissipation factor, 100Hz | 23.0 °C | 9E-3 [-] Show Material materials with Dissipation factor, 100Hz of 9E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 13 g/10min Show Material materials with Melt mass-flow rate of 13 g/10min | ISO 1133 | 250°C/2.16kg | |
Shrinkage | 23.0 °C | 1.8 % Show Material materials with Shrinkage of 1.8 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.6 % Show Material materials with Shrinkage, transverse of 1.6 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 20% Glass Bead | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |